The invention provides a method for preparing waste gas treatment material by multiple roasting, which includes the following steps: (1) soaking attapulgite with hydrochloric acid and centrifuging, roasting solid material at 200 300 C for 2 5 h to obtain acidified attapulgite; (2) mixing and grinding acidified attapulgite, activated carbon powder, redox graphene, titanium dioxide, bentonite and kaolin. (3) The step (2) first calcines the material at 300 The invention provides a method for preparing waste gas treatment material by multiple roasting method. The preparation method is simple and low cost. The powder material is mixed and roasted twice at high temperature to prepare carbon powder with high activity, which is used as waste gas treatment material.
【技术实现步骤摘要】
一种利用多次焙烧法制备废气处理材料的方法
本专利技术涉及废气处理领域，具体涉及一种利用多次焙烧法制备废气处理材料的方法。
技术介绍
废气是指人类在生产和生活过程中排出的有毒有害的气体。特别是化工厂、钢铁厂、制药厂，以及炼焦厂和炼油厂等，排放的废气气味大，严重污染环境和影响人体健康。各类生产企业排放的工业废气是大气污染物的重要来源。大量工业废气如果未经处理达标后排入大气，必然使大气环境质量下降，给人体健康带来严重危害，给国民经济造成巨大损失。工业废气中有毒有害物质可通过呼吸道和皮肤进入人体后，长期低浓度或短期高浓度接触可造成人体的呼吸、血液、肝脏等系统和器官暂时性和永久性病变，尤其是苯并芘类多环芳烃能使人体直接致癌以引起人类的高度重视。工业废气包括有机废气和无机废气。有机废气主要包括各种烃类、醇类、醛类、酸类、酮类和胺类等；无机废气主要包括硫氧化物、氮氧化物、碳氧化物、卤素及其化合物等。中国针对大气污染采取污染物排放控制制度。有机废气为主要的大气污染物之一，可通过呼吸道和皮肤进入人体，给人的呼吸、血液、肝脏等系统和器官造成暂时性和永久性病变。如PTA氧化尾气含有大量...
【技术保护点】
1.一种利用多次焙烧法制备废气处理材料的方法，其特征在于，包括以下步骤：(1)将凹凸棒土使用盐酸浸泡后离心，将固态物质于200‑300℃下焙烧2‑5h，得到酸化凹凸棒土；(2)将酸化凹凸棒土、活性炭粉、氧化还原石墨烯、二氧化钛、膨润土和高岭土混合搅拌并研磨；(3)将步骤(2)得到材料首先在300‑400℃温度条件下进行第一次焙烧，随后继续升温，在650‑700℃温度条件下进行第二次焙烧，冷却得到废气处理材料。
【技术特征摘要】
1.一种利用多次焙烧法制备废气处理材料的方法，其特征在于，包括以下步骤：(1)将凹凸棒土使用盐酸浸泡后离心，将固态物质于200-300℃下焙烧2-5h，得到酸化凹凸棒土；(2)将酸化凹凸棒土、活性炭粉、氧化还原石墨烯、二氧化钛、膨润土和高岭土混合搅拌并研磨；(3)将步骤(2)得到材料首先在300-400℃温度条件下进行第一次焙烧，随后继续升温，在650-700℃温度条件下进行第二次焙烧，冷却得到废气处理材料。2.根据权利要求1的方法，其特征在于，所述步骤(1)中盐酸的浓度为0.01-0.2mol/L。3.根据权利要求1的方法，其特征在于，所述步骤(1)中盐酸的浓度为0.1mol/L。4.根...
【专利技术属性】
技术研发人员：孙翔，沈培发，唐玉根，刘传伟，聂成成，周凤英，石金金，鄢永恒，张席，王晓庆，
申请(专利权)人：安徽蓝鼎环保能源科技有限公司，
类型：发明
国别省市：安徽,34