The invention discloses an artificial copper, which consists of raw materials with the following weight ratios: copper powder weight percentage 25 35%, bronze powder weight percentage 15 25%, epoxy resin weight percentage 35 45%, fiber weight percentage 25 35%, accelerator weight percentage 3 5%, curing agent weight percentage 2 5%, talc powder weight percentage 8 13%. The hardness of the product can reach the same composition as stone, without distortion, non-breaking, affordable price, suitable for all kinds of large and small garden landscape sculptures, indoor and outdoor can be used, non-toxic and non-radiation, solving the complex casting problems in production technology, and the sculpture performance of the product is more colorful.
【技术实现步骤摘要】
一种人造铜及其制备工艺
本专利技术涉及铜制备
，具体是一种人造铜及其制备工艺。
技术介绍
常规铸铜工艺，第一步翻模具铸蜡样，第二步修补蜡样，第三步蜡样翻砂模，沾砂模需要4到5遍，第四步等待砂模自然晾干，第五步用熔炉熔蜡模脱蜡，第六步二次蜡模加热，第七步熔铜汁，第八步把熔化好的铜汁浇注到蜡模内，第九步等待铜降温后，去除砂模外层模型，第十步产品焊接，第十一步表面打磨抛光，第十二步表面清理，经过以上十几道工序产品制作完成；以上制造技术难以掌控，生产步骤繁琐，人工成本高，材料成本高，产品过重，安装运输都不方便，生产周期过长，生产效率不高等问题。
技术实现思路
本专利技术的目的在于提供一种人造铜及其制备工艺，以解决现有技术中制造技术难以掌控，生产步骤繁琐，人工成本高，材料成本高，产品过重，安装运输都不方便，生产周期过长，生产效率不高的问题。为实现上述目的，本专利技术提供如下技术方案：一种人造铜，包括由下列重量份配比的原料组成：铜粉重量百分比25-35%，青石粉重量百分比15-25%，环氧树脂重量百分比35-45%，纤维丝重量百分比25-35%，促进剂重量百分比3-5%，固...
【技术保护点】
1.一种人造铜，其特征在于：包括由下列重量份配比的原料组成：铜粉重量百分比25‑35%，青石粉重量百分比15‑25%，环氧树脂重量百分比35‑45%，纤维丝重量百分比25‑35%，促进剂重量百分比3‑5%，固化剂重量百分比2‑5%，滑石粉重量百分比8‑13%。
【技术特征摘要】
1.一种人造铜，其特征在于：包括由下列重量份配比的原料组成：铜粉重量百分比25-35%，青石粉重量百分比15-25%，环氧树脂重量百分比35-45%，纤维丝重量百分比25-35%，促进剂重量百分比3-5%，固化剂重量百分比2-5%，滑石粉重量百分比8-13%。2.根据权利要求1所述的一种人造铜的制备工艺，其特征在于：包括以下步骤：S1：材料准备：裁毡和调制铜粉；S2：模具准备：将模具清洗干净；S3：将模具打蜡；S4：上脱模剂；S5：将调整好的材料手糊成型；S6：固化脱模；S7：产品处理：打磨抛光；S8：检查产品。3.根据权利要求2所述的...
【专利技术属性】
技术研发人员：朱红兵，李政，刘凯，
申请(专利权)人：苏州中阑文化科技有限公司，
类型：发明
国别省市：江苏,32