The invention belongs to the technical field of cement processing, in particular to a cement made by recycling construction waste and a manufacturing method thereof. The invention comprises the following weight parts of raw materials: 60-70 parts of limestone, 30-40 parts of construction waste, 3-5 parts of gypsum, 10-15 parts of iron ore slag, 9-14 parts of fly ash, 20-30 parts of clay and 0.2-0.4 parts of cement additives. The invention recycles building wastes of concrete structure, marble damaged building wastes, concrete blocks, brick and tile fragments and waste mortar as raw materials for cement production, which can effectively save production costs, reduce waste of resources, and effectively reduce environmental pollution problems caused by building waste accumulation.
【技术实现步骤摘要】
一种建筑废料回收制作的水泥及其制作方法
本专利技术属于水泥加工
，具体涉及一种建筑废料回收制作的水泥及其制作方法。
技术介绍
随着工业化、城市化进程的加速，建筑业也同时快速发展，相伴而产生的建筑垃圾日益增多，中国建筑垃圾的数量已占到城市垃圾总量的1/3以上。截至2011年，中国城市固体生活垃圾存量已达70亿吨，可推算建筑垃圾总量为21亿至28亿吨，每年新产生建筑垃圾超过3亿吨。如采取简单的堆放方式处理，每年新增建筑垃圾的处理都将占1.5亿至2亿平方米用地。中国正处于经济建设高速发展时期，每年不可避免地产生数亿吨建筑垃圾。如果不及时处理和利用，必将给社会、环境和资源带来不利影响。随着城市建筑垃圾量的增加，垃圾堆放点也在增加，而垃圾堆放场的面积也在逐渐扩大。垃圾与人争地的现象已到了相当严重的地步，大多数郊区垃圾堆放场多以露天堆放为主，经历长期的日晒雨淋后，垃圾中的有害物质(其中包含有城市建筑垃圾中的油漆、涂料和沥青等释放出的多环芳烃构化物质)通过垃圾渗滤液渗入土壤中，从而发生一系列物理、化学和生物反应，如过滤、吸附、沉淀，或为植物根系吸收或被微生物合成吸收，造成...
【技术保护点】
1.一种建筑废料回收制作的水泥，其特征在于，包括以下重量份原料：石灰石60～70份、建筑废料30～40份、石膏3～5份、铁矿渣10～15份、粉煤灰9～14份、黏土20～30份、水泥助剂0.2～0.4份。
【技术特征摘要】
1.一种建筑废料回收制作的水泥，其特征在于，包括以下重量份原料：石灰石60～70份、建筑废料30～40份、石膏3～5份、铁矿渣10～15份、粉煤灰9～14份、黏土20～30份、水泥助剂0.2～0.4份。2.根据权利要求1所述的一种建筑废料回收制作的水泥，其特征在于，包括以下重量份原料：石灰石64份、建筑废料30份、石膏3份、铁矿渣12份、粉煤灰14份、黏土26份、水泥助剂0.2份。3.根据权利要求1或2所述的一种建筑废料回收制作的水泥，其特征在于，所述建筑废料包括：混凝土结构的建筑废料、大理石破损建筑废料、混凝土块、砖瓦碎块和废砂浆等。4.根据权利要求1或2所述的一种建筑废料回收制作的水泥，其特征在于，所述水泥助剂的为丙三醇、氯化钾、硝酸钠、酒石酸和环氧树脂按质量比(2～3):(4～6):(1～3):(2～3):(1～3)混合均匀制得。5.一种建筑废料回收制作水泥的方法，其特征在于，包括以下步骤：a、将建筑垃圾分类回收，选出生活垃圾和墙体钢筋等杂物，得到...
【专利技术属性】
技术研发人员：王冬，冯宗林，钟继，
申请(专利权)人：贵州长泰源节能建材股份有限公司，
类型：发明
国别省市：贵州,52