Surface T-treatment of Ceramic Matrix

The invention relates to a T-treatment method for ceramic matrix surface, which comprises the following steps: step 1, cleaning the ceramic matrix surface with a cleaning solution; step 2, treating the ceramic matrix in alkali solution; step 3, pretreatment of the ceramic matrix in acid solution containing dilute sulfuric acid; step 4, soaking and corrosion of the ceramic matrix in a mixed solution of hydrochloric acid and phosphoric acid; step 5, and step 3. Ceramic matrix is protected in polyvinyl phosphate. The beneficial effect of the invention is that the ceramic component and the resin component are joined by chemical means to complete the integration of the two materials.

【技术实现步骤摘要】
陶瓷基体表面T处理方法
本专利技术涉及陶瓷表面处理
，特别涉及一种陶瓷基体表面T处理方法。
技术介绍
现在市场使用的陶瓷与树脂的结合主要依赖于陶瓷产品的结构或完全避开不使用陶瓷，目前手机行业中后盖材质主要使用金属、塑料、玻璃。使用金属后盖容易对信号造成干扰、所以一般金属都无法做到机身一体化、另外一般金属是没有颜色的，为了美观，一般使用电镀、阳极或喷漆，不仅工艺复杂、不环保，且长期使用过程中也会出现掉色、腐蚀等现象。由于塑料比较软，容易刮花及变形，时间长了颜色也会变深，影响美观。玻璃不易刮花，但是易碎；陶瓷的优势在于耐磨耐刮，也不容易摔碎，又不会像金属对信号有干扰等问题，外观在长期使用过程中也不会掉色、腐蚀。
技术实现思路
本专利技术的目的是通过陶瓷构件与树脂构件的接合，完成两种材料一体化，是通过如下技术方案实现的。陶瓷基体表面T处理方法，包含以下处理步骤：步骤1、用清洗液对陶瓷基体表面进行清洗处理；步骤2、将陶瓷基体放入碱液中处理；步骤3、将陶瓷基体放在含有稀硫酸的酸液中预处理；步骤4、将陶瓷基体在盐酸与磷酸的混合溶液中浸泡、腐蚀；步骤5、陶瓷基体在聚烯基磷酸酯中进行保护处理。进一本文档来自技高网...

【技术保护点】
1.陶瓷基体表面T处理方法，其特征在于，包含以下处理步骤：步骤1、用清洗液对陶瓷基体表面进行清洗处理；步骤2、将陶瓷基体放入碱液中处理；步骤3、将陶瓷基体放在含有稀硫酸的酸液中预处理；步骤4、将陶瓷基体在盐酸与磷酸的混合溶液中浸泡、腐蚀；步骤5、陶瓷基体在聚烯基磷酸酯中进行保护处理。

【技术特征摘要】
1.陶瓷基体表面T处理方法，其特征在于，包含以下处理步骤：步骤1、用清洗液对陶瓷基体表面进行清洗处理；步骤2、将陶瓷基体放入碱液中处理；步骤3、将陶瓷基体放在含有稀硫酸的酸液中预处理；步骤4、将陶瓷基体在盐酸与磷酸的混合溶液中浸泡、腐蚀；步骤5、陶瓷基体在聚烯基磷酸酯中进行保护处理。2.根据权利要求1所述的陶瓷基体表面T处理方法，其特征在于，所述步骤1中，具体是将陶瓷基体在质量浓度为45～55g/L的磷酸钠、碳酸钠及焦磷酸钠混合溶液的脱脂剂溶液中浸泡5-8分钟，温度50-60℃。3.根据权利要求1所述的陶瓷基体表面T处理方法，其特征在于，所述碱溶液是NAOH溶液中，NAOH浓度40-6...