The invention discloses a development method of waste acid reduction technology for hot-dip pickling, which includes neutralization, flocculation and precipitation, plate-frame pressure filtration, three-effect concentration, centrifugal separation, high-temperature calcination, three-effect evaporation condensate for workshop reuse, centrifugal separation to produce sodium chloride into chlor-alkali industry, and high-temperature calcination to send ore powder to iron and steel industry. The technology has stable operation. It has good treatment effect, no secondary pollution, can turn waste into treasure, realize the comprehensive utilization of waste acid, and can be applied in industrial production.
【技术实现步骤摘要】
一种热镀酸洗废酸减量化技术的开发方法
本专利技术涉及热镀酸洗废酸减量化
，属于危废减量化及其资源化利用的范畴，具体为一种热镀酸洗废酸减量化技术的开发方法。
技术介绍
热镀是一种有效的金属防腐技术，现已应用于各行业金属防腐结构设施上。热镀过程需要将金属设备表面进行酸洗浸泡，用来增加金属的附着力。随着酸溶液除锈次数的不断增加，酸溶液中金属离子浓度不断增加，酸浓度不断降低，此时的酸已经失去了酸洗的价值，此酸会作为废酸。在我国《国家危险废物名录》中明确规定，此废酸需要作为危险废物进行处置不能直接排放，且处置费用相当高，一直是制约该行业发展的主要瓶颈之一。目前国内针对此种废酸，主要采取酸碱中和或者盐酸回收处理的方式进行处置。酸碱中和过程能够有效的将废酸中和成中性，但是中和后的废酸转化成饱和食盐水废水。废水中的铁离子虽然沉淀出来，该部分铁泥任然属于危废，会有二次污染，且中和后废水中盐含量较高，排放容易造成土壤盐碱化。盐酸回收技术主要是利用盐酸在加热状态容易挥发的特性，在加热状态下将废酸中的盐酸挥发出来，通过冷凝处理，回收盐酸，该技术的不足之处在于，回收盐酸的浓度不高，运...
【技术保护点】
1.一种热镀酸洗废酸减量化技术的开发方法，其特征在于：包括以下步骤：步骤一：使用碱性调节剂调节废水pH至7.0～9.0，沉淀后加入助凝剂进行絮凝反应；步骤二：通过螺杆泵将絮凝后混合液打入板框压滤机中压滤，压滤出水引入调节池中，固体泥饼运至干燥区域；步骤三：将泥饼送至炉膛内煅烧，煅烧温度为500～600℃，煅烧后黑色固体为铁矿粉，送至干铁厂进行炼钢使用；步骤四：调节池内液体送至三效蒸发装置中，三效蒸发温度为60.0～100.0℃，蒸馏冷凝液回用至热镀车间，釜底残渣为氯化钠，离心后送至氯碱厂。
【技术特征摘要】
1.一种热镀酸洗废酸减量化技术的开发方法，其特征在于：包括以下步骤：步骤一：使用碱性调节剂调节废水pH至7.0～9.0，沉淀后加入助凝剂进行絮凝反应；步骤二：通过螺杆泵将絮凝后混合液打入板框压滤机中压滤，压滤出水引入调节池中，固体泥饼运至干燥区域；步骤三：将泥饼送至炉膛内煅烧，煅烧温度为500～600℃，煅烧后黑色固体为铁矿粉，送至干铁厂进行炼钢使用；步骤四：调节池内液体送至三效蒸发装置中，三效蒸发温度为60.0～100.0℃，蒸馏冷凝液回用至热镀车间，釜底残渣为氯化钠，离心后送至氯碱厂。2.根据权利要求1所述的一种热镀酸洗废酸减量化技术的开发方法，其特征在于：所述步骤一中碱性调节剂为NaOH，助凝剂为阳离子聚丙烯酰胺。3.根据权利要求2所述的一种热镀酸洗废酸减量...
【专利技术属性】
技术研发人员：陈金贵，林定多，
申请(专利权)人：江苏道明化学有限公司，
类型：发明
国别省市：江苏,32