一种用于电缆材料的复合橡胶制造技术

本发明专利技术提供一种用于电缆材料的复合橡胶，按照重量份数，包括如下组分：氯丁橡胶35‑50份，AES树脂15‑20份，气相二氧化硅5‑8份，硅烷偶联剂1‑2份，抗氧剂2‑3份，二硫化钼3‑5份，油酸3‑5份，丁晴橡胶30‑40份，碳酸钙6‑10份，尼龙算二辛脂10‑15份，不溶性硫磺2‑5重量份，TAIC‑70 1‑5重量份。本发明专利技术的用于电缆材料的复合橡胶为非极性高聚物，具有弹性柔软和抗磨损等特性，能够适应‑50～65℃的极端恶劣环境，随环境温度的不断降低，不会明显硬化而失去柔软性和弹性。

A Composite Rubber for Cable Materials

The invention provides a composite rubber for cable materials, which comprises 35 50 copies of chloroprene rubber, 15 20 copies of AES resin, 5 8 copies of fumed silica, 1 2 copies of silane coupling agent, 2 3 copies of antioxidant, 3 5 copies of molybdenum disulfide, 3 5 copies of oleic acid, 30 40 copies of butadiene rubber, 6 10 copies of calcium carbonate, 10 15 copies of nylon, insolubility. Sulfur 2 5 by weight and TAIC 70 1 5 by weight. The composite rubber used for cable material of the invention is a non-polar polymer, has the characteristics of elasticity, softness and wear resistance, can adapt to the extreme harsh environment of

【技术实现步骤摘要】
一种用于电缆材料的复合橡胶
本专利技术设计电缆材料
，具体涉及一种用于电缆材料的复合橡胶。
技术介绍
电线电缆绝缘及护套用塑料俗称电缆料，其中包括了橡胶、塑料、尼龙等多种品种。电缆料生产企业是以电缆生产企业为用户，只要有电线电缆需求就有电缆料的市场。电线电缆产品中除钢芯铝绞线、电磁线等裸线产品外几乎都需要绝缘层口。目前我国有电线电缆生产企业近5000家，又有城乡电网改造、西部大开发及通信设施大面积升级改造对电线电缆产品的巨大需求，因而从一段时间来看，电缆料在我国具有广泛的市场发展前景。现有技术中，风力电站风筒软电缆的护套采用的橡胶主要有：天然橡胶(NR)、天然橡胶和丁苯橡胶的二元复合橡胶(NR-SBR)、氯化聚乙烯(CPE)、氯丁橡胶(CR)、硫化型丁腈橡胶和聚氯乙烯的复合物(NBR-PVC)，也有个别用热塑性NBR-PVC复合物。NR和NR-SBR两种橡胶虽然耐低温性能满足实际需要，但其弹性不理想，耐磨性也待提高。CPE、CR、NBR-PV等材料均为极性高聚物，随温度下降分子间次价力增长很快，至-25℃以下均变为僵硬，丧失弹性，电缆旋转困难并产生开裂，不能适应-35℃和更低温本文档来自技高网...

【技术保护点】
1.一种用于电缆材料的复合橡胶，其特征在于，按照重量份数，包括如下组分：氯丁橡胶35‑50份，AES树脂15‑20份，气相二氧化硅5‑8份，硅烷偶联剂1‑2份，抗氧剂2‑3份，二硫化钼3‑5份，油酸3‑5份，丁晴橡胶30‑40份，碳酸钙6‑10份，尼龙算二辛脂10‑15份。

【技术特征摘要】
1.一种用于电缆材料的复合橡胶，其特征在于，按照重量份数，包括如下组分：氯丁橡胶35-50份，AES树脂15-20份，气相二氧化硅5-8份，硅烷偶联剂1-2份，抗氧剂2-3份，二硫化钼3-5份，油酸3-5份，丁晴橡胶30-40份，碳酸钙6-10份，尼龙算二辛脂10-15份。2.根据权利要求1所述的一种用于电缆材料的复合橡胶，其特征在于，所述复合橡胶还包括不溶性硫磺2-5重量份。3.根据权利要求1所述的一种用于电缆材料的复合橡胶，其特征在于，所述复合橡胶还包括TAIC-701-5重量份。4.根据权利要求1所述...

【专利技术属性】
技术研发人员：程江，
申请(专利权)人：上海电缆厂南京有限公司，
类型：发明
国别省市：江苏,32