The invention relates to a capsule rubber for transformers, which comprises 100 parts of nitrile rubber, 69 parts of carbon black, 19 21 parts of plasticizer, 2.9 3.1 parts of graphene oxide, 4.9 5.1 parts of activator, 0.9 1.1 parts of stearic acid, 1.9 2.1 parts of antioxidant, 0.9 1.1 part of sulfur, 4.4 parts of vulcanization accelerator. The invention adopts oil-resistant nitrile-butadiene rubber with excellent oil resistance, and focuses on improving oil resistance and heat aging resistance. The addition of graphene oxide increases the dispersion of nitrile-butadiene rubber fillers, improves the mechanical properties, high barrier performance and high aging resistance of nitrile-butadiene rubber, and greatly prolongs the service life of capsule rubber.
【技术实现步骤摘要】
一种用于变压器的胶囊胶料
本专利技术涉及材料领域，特别是涉及一种用于变压器的胶囊胶料。
技术介绍
储油柜是用于变压器的一种储油装置，当变压器油的体积随着油温的变化而膨胀或缩小时，储油柜起储油和补油作用，能保证油箱内充满油，使变压器与空气的接触面减小，且从空气中吸收的水分、灰尘和氧化后的油垢都沉积在储油柜底部的沉积器中，从而大大减缓变压器油的劣化速度。储油柜主要有三种形式：波纹式、胶囊式、隔膜式。对于胶囊式储油柜，由于胶囊胶料接触变压器油，对力学性能、阻隔性能和耐老化性能要求极高。行业现有的胶囊胶料性能不佳，会导致胶囊寿命的缩短。
技术实现思路
本专利技术的目的是提供一种高力学性能、高阻隔性能和高耐老化性的用于变压器的胶囊胶料。本专利技术通过如下技术方案实现上述目的：一种用于变压器的胶囊胶料，包括以下重量份数的组分：丁腈橡胶100份；炭黑69-71份；增塑剂19-21份；氧化石墨烯2.9-3.1份；活化剂4.9-5.1份；硬脂酸0.9-1.1份；防老剂1.9-2.1份；硫磺0.9-1.1份；硫化促进剂4-4.4份。进一步的，所述炭黑为HAF炭黑。进一步的，所述增塑剂为T...
【技术保护点】
1.一种用于变压器的胶囊胶料，其特征在于，包括以下重量份数的组分：丁腈橡胶 100份；炭黑 69‑71份；增塑剂 19‑21份；氧化石墨烯 2.9‑3.1份；活化剂 4.9‑5.1份；硬脂酸 0.9‑1.1份；防老剂 1.9‑2.1份；硫磺 0.9‑1.1份；硫化促进剂 4‑4.4份。
【技术特征摘要】
1.一种用于变压器的胶囊胶料，其特征在于，包括以下重量份数的组分：丁腈橡胶100份；炭黑69-71份；增塑剂19-21份；氧化石墨烯2.9-3.1份；活化剂4.9-5.1份；硬脂酸0.9-1.1份；防老剂1.9-2.1份；硫磺0.9-1.1份；硫化促进剂4-4.4份。2.根据权利要求1所述的用于变压器的胶囊胶料，其特征在于：所述炭黑为HAF炭黑。3.根据权利要求1所述的用于变压器的胶囊胶料，其特征在于：所述增塑剂为TP-95增塑剂。4.根据权利要求1所述的用于变压器的胶囊胶料，其特征在于：所述活化剂为氧化锌。5.根据权利要求1所述的用于变压器的胶囊胶料，其特征在于：所述防老剂为防老剂4010NA。6.根据权利要求1所述的用于变压器的胶囊胶料，其特征在于：所述硫化促进剂包括促进剂CBS、促进剂DPTT和促进剂TMTD。7.一种用于变压器的胶囊胶料的制备方法，其特征在于，包括以下步骤：S1、秤料：秤取丁腈橡胶100份、炭黑69-71份、增塑剂19-21份、氧化石墨烯2.9-3...
【专利技术属性】
技术研发人员：朱宣杭，马小兵，冯宇，
申请(专利权)人：南通世睿电力科技有限公司，
类型：发明
国别省市：江苏,32