The invention discloses a method for synthesizing polycarbosilane, which comprises the following steps: in inert atmosphere, using tri (pentafluorophenyl) borane (B (C6F5) 3) as catalyst, polymerizing vinyl hydrosilane monomers in organic solvents to obtain polycarbosilane; or in inert atmosphere, using B (C6F5) 3 as catalyst, divinyl compounds and dihydrosilane compounds in organic solvents. Polycarbosilane was synthesized by polymerization. Compared with the traditional preparation methods, the products prepared by this method have a remarkable improvement in anti-aging caused by residual metal catalysts, especially in the fields of biology, electronics (such as etching) and optics, which require no toxic side effects and no residual component effects.
【技术实现步骤摘要】
一种聚碳硅烷的合成方法
本专利技术涉及碳硅烷
，尤其涉及一种聚碳硅烷的合成方法。
技术介绍
硅-氢加成反应是目前用来制备碳硅烷的通用方法。自1947年Sommer等人发现以来,已成为有机硅化学中研究盛行、应用极广的一个反应。不同于难被活化的碳-氢σ键，硅-氢σ键可被某些过渡金属催化剂轻易活化，被活化的硅-氢键能很好地与羰基、氰基、烯烃、炔烃等含多重键的化合物进行氢硅烷化加成反应而得到目标产物。例如，对羰基与氰基等官能团进行硅-氢加成，可使该类官能团在温和条件下转化为醇和胺类化合物；对C=C或C≡C进行硅-氢加成，则可得到水解稳定性好的硅碳键,使得该类反应在硅单体、偶联剂、硅橡胶和许多含硅高分子的制备中得到广泛应用。在高分子合成方面，氢硅烷化反应常被用做从乙烯基硅烷单体直接合成聚碳硅烷；所得聚合物具有低的玻璃化转变温度，是常用的弹性体材料的添加剂。截至目前，采用过渡贵金属化合物为催化剂合成聚碳硅烷仍为最常用制备方法。例如，采用Karstedt催化剂（一种含铂(0)的催化剂，结构式如下）催化1,3-双(二甲基乙烯基硅烷基)苯与1,3-双(二甲基硅烷基)苯的共聚加...
【技术保护点】
1. 一种聚碳硅烷的合成方法，其特征在于，包括如下步骤：在惰性气氛中，以 B(C6F5)3 为催化剂、在有机溶剂中将乙烯基氢硅烷类单体聚合，得到聚碳硅烷；或者，在惰性气氛中，以 B(C6F5)3 为催化剂、在有机溶剂中将双乙烯基化合物与双氢硅烷化合物进行聚合，得到聚碳硅烷。
【技术特征摘要】
1.一种聚碳硅烷的合成方法，其特征在于，包括如下步骤：在惰性气氛中，以B(C6F5)3为催化剂、在有机溶剂中将乙烯基氢硅烷类单体聚合，得到聚碳硅烷；或者，在惰性气氛中，以B(C6F5)3为催化剂、在有机溶剂中将双乙烯基化合物与双氢硅烷化合物进行聚合，得到聚碳硅烷。2.根据权利要求1所述的聚碳硅烷的合成方法，其特征在于，具体包括如下步骤：将各原料分散于有机溶剂中，于室温下进行搅拌聚合，最后进行再沉淀提纯，得到聚碳硅烷。3.根据权利要求2...
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。