The invention relates to the technical field of feldspar purification, and discloses a processing method for inferior feldspar ore, which includes the following steps: S1. Crushing inferior feldspar ore to obtain feldspar particles; S2. Reducing feldspar particles obtained in the process of reduction reaction, the reducing agent is carbon monoxide; S3. Ball milling, magnetic separation, iron removal, pressure filtration and drying of feldspar particles reacted in step 2, and the most important step is to reduce feldspar particles. Final feldspar powder. In view of the inferior feldspar ore which can not be treated by conventional process, the present invention creatively uses carbon monoxide as reducing agent to reduce the iron oxide in the original inferior feldspar ore to ferric oxide at high temperature, thereby processing inferior feldspar into high quality feldspar which can be processed by conventional process.
【技术实现步骤摘要】
一种劣质长石矿加工方法及其长石精粉
本专利技术涉及长石提纯
，更具体地，涉及一种劣质长石矿加工方法。
技术介绍
长石是钾、钠、钙、钡等碱金属或碱土金属的铝硅酸盐矿物，晶体结构属架状结构。其主要化学成分为SiO2、Al2O3、K2O、Na2O、CaO等。长石族矿物是地壳中分布最广的矿物，约占地壳总重量的50%，是一种普遍存在的造岩矿物。60%的长石赋存在岩浆岩中，30%分布在变质岩中，10%存在于沉积岩碎屑岩中，但只有在相当富集时长石才能成为工业矿物。长石矿物富含钾、钠等碱金属，熔融温度较低(1100～1200℃)，熔融间隔较长，具有较强的助熔性和较高的化学稳定性。我国长石资源很丰富，以钾长石为主，但是能够满足工业要求的优质长石矿较少，绝大部分都含有石英、白云母、黑云母、金红石、磁铁矿、赤铁矿、褐铁矿，有些长石原矿中还含有磷灰石、黄铁矿、榍石、角闪石、电气石等，含铁量比较高，而且铁结构也非常复杂，极大增加了除铁难度，因而采用常规工艺，长石白度或烧成白度达不到要求。为了提高长石的工业价值，满足工业对优质长石矿的需求，必须从劣质长石矿中去除杂质矿物，尤其是对铁的去...
【技术保护点】
1.一种劣质长石矿加工方法，其特征在于，包括以下步骤：S1.将劣质长石矿进行破碎，得到长石矿颗粒；S2.将步骤S1中得到的长石矿颗粒进行还原反应，还原剂为一氧化碳；S3.将步骤S2中反应后的长石矿颗粒依次球磨、磁选除铁、压滤、烘干，最终得到长石精粉。
【技术特征摘要】
1.一种劣质长石矿加工方法，其特征在于，包括以下步骤：S1.将劣质长石矿进行破碎，得到长石矿颗粒；S2.将步骤S1中得到的长石矿颗粒进行还原反应，还原剂为一氧化碳；S3.将步骤S2中反应后的长石矿颗粒依次球磨、磁选除铁、压滤、烘干，最终得到长石精粉。2.根据权利要求1所述劣质长石矿加工方法，其特征在于，步骤S1中所述劣质长石矿通过破碎机进行破碎。3.根据权利要求1所述劣质长石矿加工方法，其特征在于，步骤S2中所述还原温度为300～900℃。4.根据权利要求1所述劣质长石矿加工方法，其特征在于，步骤S2中所...
【专利技术属性】