本发明专利技术公开了一种介入性医疗器械的激光表面处理方法，涉及激光技术应用领域，主要是利用激光扫描，在介入性医疗器械的表面形成可降低其在人体通道中时与人体通道间的摩擦力的微结构，从而降低了表面摩擦，而可以免除在介入性医疗器械的表面形成用于减小摩擦的镀层，排除了镀层脱落而危害患者的风险，从而使得介入性手术更为安全、可靠。

A Laser Surface Processing Method for Interventional Medical Devices

The invention discloses a laser surface treatment method for interventional medical devices, which relates to the application field of laser technology, mainly using laser scanning to form a micro-structure on the surface of interventional medical devices that can reduce the friction force between them and human channels when they are in human channels, thereby reducing the surface friction, and can be exempted from the surface formation of interventional medical devices for reduction. Small friction coating eliminates the risk of coating falling off and endangering patients, thus making interventional surgery safer and more reliable.

【技术实现步骤摘要】
一种介入性医疗器械的激光表面处理方法
本专利技术涉及激光应用
，尤其是指一种介入性医疗器械的激光表面处理方法。
技术介绍
现有技术中，介入性医疗器械在工作中，需要在人体通道内(如血管，或各种肠道)移动。为了减轻介入性医疗器械与人体通道内之间的摩擦力，一般需于介入性医疗器械的表面镀上一涂层，以改善器械在人体通道内的移动性和操作性。但是，该种涂层增加了额外的风险，即涂层有剥落的可能性。剥落的涂层会遗留在人体通道内，严重时甚至会导致病患死亡。
技术实现思路
本专利技术所要解决的技术问题是：如何降低介入性医疗器械在人体通道间的摩擦，以替代可能脱落的涂层处理方法。为了解决上述技术问题，本专利技术公开了一种介入性医疗器械的激光表面处理方法，具体为：获取激光表面处理所用激光束，将激光束聚焦于介入性医疗器械的待处理表面，控制激光束在介入性医疗器械待处理表面的相对位置的变化和激光处理时间，在介入性医疗器械的表面形成可减小与人体通道间接触时摩擦力的微结构。在进一步的方案中，所述微结构为接触角大于150度的疏水结构。在进一步的方案中，所述微结构为接触角小于30度的亲水结构。在进一步的方案中，通过控制激光本文档来自技高网...

【技术保护点】
1.一种介入性医疗器械的激光表面处理方法，其特征在于:获取激光表面处理所用激光束，将激光束聚焦于介入性医疗器械的待处理表面，控制激光束在介入性医疗器械待处理表面的相对位置的变化和激光处理时间，在介入性医疗器械的表面形成可减小与人体通道间接触时摩擦力的微结构。

【技术特征摘要】
1.一种介入性医疗器械的激光表面处理方法，其特征在于:获取激光表面处理所用激光束，将激光束聚焦于介入性医疗器械的待处理表面，控制激光束在介入性医疗器械待处理表面的相对位置的变化和激光处理时间，在介入性医疗器械的表面形成可减小与人体通道间接触时摩擦力的微结构。2.如权利要求1所述的介入性医疗器械的激光表面处理方法，其特征在于:所述微结构为接触角大于150度的疏水结构。3.如权利要求1所述的介入性医疗器械的激光表面处理方法，其特征在于:所述微结构为接触角小于30度的亲水结构。4.如权利要求2或3所述的介入性医疗器械的激光表面处理方法，其特征在于:通过控制激光束的移动或待处理介入性医疗器械表面的移动，来控制激光束聚焦在待处理表面上的相对位置。5.如权利要求4...