The invention discloses a free forging method for large size Ti55531 titanium alloy bars, which is realized by open forging dynamic recrystallization heat treatment processing forging below beta transition temperature. On the basis of the conventional free forging process route, the Ti55531 billet is rapidly refined by means of the recrystallization heat treatment process after the initial forging process, which solves the problem that the large size grains need to be broken by multiple fires and large deformation during the conventional free forging process, and achieves the purpose of reducing the forging production cost.
【技术实现步骤摘要】
Ti55531钛合金大规格棒材自由锻造方法
本专利技术提供一种Ti55531钛合金大规格棒材自由锻造方法，属于钛合金材料加工
技术介绍
Ti55531合金名义成分为Ti-5Al-5Mo-5V-3Cr-1Zr，是一种新型的高强高韧近β钛合金，具有极佳的强度、塑性与韧性匹配性，热成型性能较好，并且具有良好的淬透性，与当前广泛应用于大型民用客机上的Ti1023合金相比，Ti55531合金不会产生明显的成分偏析，且室温抗拉强度提高了约15%。该合金主要替代TC4与Ti1023等合金，应用于飞机起落架、机翼等承力结构件，性能要求在兼顾高强与高韧的同时具有一定的塑性。近年来随着材料的发展以及能源危机的冲击，航空航天工业对高强度、高韧性、低密度、价格低廉的新型结构材料的需要越来越迫切。因此，低成本新型钛合金便成为近年来新材料的研究热点，Ti55531钛合金首当其冲成为钛合金研究领域的热点。本申请针对航空航天工业对钛合金大规格棒材的应用需求，开展Φ400~Φ500mm棒材加工技术研究，实现Ti55531钛合金大规格棒材的低成本、规模化稳定生产，满足航空航天工业发展的需要...
【技术保护点】
1.Ti55531钛合金大规格棒材自由锻造方法，其特征在于，经开坯锻造→动态再结晶热处理加工→β转变温度以下锻造来实现。
【技术特征摘要】
1.Ti55531钛合金大规格棒材自由锻造方法，其特征在于，经开坯锻造→动态再结晶热处理加工→β转变温度以下锻造来实现。2.根据权利要求1所述的Ti55531钛合金大规格棒材自由锻造方法，其特征在于，根据权利要求1所述的Ti55531钛合金大规格棒材自由锻造方法，其特征在于，具体的工艺流程如下：（一）开坯锻造将Ti55531钛合金铸锭在β转变温度以上250℃～350℃进行1～2火次的镦拔锻造，每火次锻造比控制在2.1～3.5之间，锻后均采用空冷；（二）动态再结晶热处理加工加热温度在β转变温度以下30℃~50℃，对经过步骤（一）处理的坯料进行1次镦拔锻造，锻造比控制在1.4～1.8之间，锻后直接回炉进行再结晶热处理且热处理加热温度在β转变温度以上80℃~100℃，保温适当时间后出炉，然后进行1次镦拔锻造，锻造比控制在1.1～1.3之间，锻后采用空冷；（三）β转变温度以下锻造先对经过步骤（二）处理的坯料进行1～3火次的镦拔锻造且加热温度在β转变温度以下30℃~5...
【专利技术属性】
技术研发人员：朱雪峰，樊凯，黄德超，彭晖，
申请(专利权)人：湖南金天钛业科技有限公司，
类型：发明
国别省市：湖南,43
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。