The invention discloses a composite material used for manufacturing glass crafts. Its raw material composition and corresponding weight components are: silica sand 25-35 phr, kaolin 22-24 phr, limestone 20-26 phr, sodium carbonate 17-22 phr, sodium sulfate 12-16 phr, phthalic acid 8-12 phr, glass colorant 3-6 phr, polystyrene 1-4 phr, polyvinyl acetate 1-4 phr, basic copper carbonate 4-8 phr. Copper oxide 2-4 phr, vinyl resin 1-2 phr. The glass handicraft prepared by the composite material used for manufacturing glass handicraft has the characteristics of light weight, high strength and strong corrosion resistance, and is convenient for transportation and preservation of glass handicraft.
【技术实现步骤摘要】
一种用于玻璃工艺品的新型复合材料
本专利技术涉及玻璃工艺品材料
,具体领域为一种用于制造玻璃工艺品的复合材料。
技术介绍
玻璃工艺品一般分为熔融玻璃工艺品、灯工玻璃工艺品、琉璃工艺品三大类,常作为装饰材料或高档礼品及艺术品,玻璃工艺品的制作工艺大多为手工制胎、雕刻、用脱腊铸造法,经多次翻模,浇注成型,如灯工玻璃工艺品是以五颜六色的玻璃棒为主要材料,运用氧气与液化气给玻璃棒加热,使加热后的棒材快速融化,然后由操作工借助钳子、刀片等其他小工具进行各款产品塑形的全过程操作,随社会不断发展,人们的品味逐渐提高,越发注重精神生活,比玻璃工艺品由此受到人们的青睐,其可以提升家里装饰的品味与艺术感,现有用于制造玻璃工艺品的复合材料与普通玻璃的原材料组成相差无几,制备出的玻璃工艺品质量较大、易碎、不耐腐蚀,导致不易运输和保存,为此提出一种用于制造玻璃工艺品的复合材料。
技术实现思路
本专利技术的目的在于提供一种用于玻璃工艺品的新型复合材料,以解决上述
技术介绍
中提出的问题。为实现上述目的,本专利技术提供如下技术方案:一种用于制造玻璃工艺品的复合材料,其原材料组成和相应的重量份数为:硅砂25~35份、高岭土22~24份、石灰石20~26份、碳酸钠17~22份、硫酸钠12~16份、邻苯二甲酸8~12份、玻璃着色剂3~6份、聚苯乙烯1~4份、聚乙酸乙烯酯1~4份、碱式碳酸铜4~8份、氧化亚铜2~4份,乙烯基树脂1~2份。优选的,所述硅砂中二氧化硅含量为95%~98%。优选的,所述高岭土中三氧化二铝的含量至少为25%。优选的,所述石灰石中氧化钙的含量至少为50%。与现有技术相比, ...
【技术保护点】
1.一种用于制造玻璃工艺品的复合材料,其特征在于:其原材料组成和相应的重量份数为:硅砂25~35份、高岭土22~24份、石灰石20~26份、碳酸钠17~22份、硫酸钠12~16份、邻苯二甲酸8~12份、玻璃着色剂3~6份、聚苯乙烯1~4份、聚乙酸乙烯酯1~4份、碱式碳酸铜4~8份、氧化亚铜2~4份,乙烯基树脂1~2份。
【技术特征摘要】
1.一种用于制造玻璃工艺品的复合材料,其特征在于:其原材料组成和相应的重量份数为:硅砂25~35份、高岭土22~24份、石灰石20~26份、碳酸钠17~22份、硫酸钠12~16份、邻苯二甲酸8~12份、玻璃着色剂3~6份、聚苯乙烯1~4份、聚乙酸乙烯酯1~4份、碱式碳酸铜4~8份、氧化亚铜2~4份,乙烯基树脂1~2份。2....
【专利技术属性】
技术研发人员:吴迪,
申请(专利权)人:嘉兴保利文化创意有限公司,
类型:发明
国别省市:浙江,33