The invention provides a palladium-supported solid catalyst, which comprises a carrier, the carrier is a cation exchange resin, the uniformity coefficient of the cation exchange resin is less than 1.1, and the active component is a precious metal palladium, which is distributed in the form of a single substance in the carrier. The palladium supported solid catalyst of the invention improves the environmental temperature of the existing catalytic hydrogenation technology for eliminating dissolved oxygen in water from 40 to 70, improves the thermal stability, widens the application scope, and the deoxidization performance will not change.
【技术实现步骤摘要】
一种钯负载固体催化剂及其制备方法
本专利技术涉及一种钯负载固体催化剂及其制备方法。
技术介绍
在常温常压下，水中会溶有一定量的氧气，溶解氧浓度一般为8～10mg/L。在核电站除盐水、锅炉给水及半导体等超纯水应用领域中，高浓度的溶解氧会加重设备的腐蚀，从而缩短设备的使用寿命，影响产品质量，严重情况下可引发事故。因此，工业应用中严格限制水中溶解氧浓度，比如核电站除盐水系统不能超过20μg/L，甚至低于10μg/L；《GB1576-2008工业锅炉水质》中规定：额定蒸发量大于或等于10t/h的锅炉，给水应除氧，含氧量小于或等于0.05mg/L。传统的溶解氧去除方法有热力除氧、真空除氧、解吸除氧、化学除氧等，但是无论哪种方法，都由于自身的缺陷而存在一定的局限性，不是会使处理后的水质发生变化(如含肼而有毒性；增加CO2含量而降低pH值；增加水的干燥余量；或产生二价铁)，就是要求高位布置或占地面积大，或是操作复杂、运行费用高。一般认为大气式热力除氧效果较为稳定，对水质无影响，但仍要求高位布置；需要大量蒸汽，运行费用较高。上世纪60年代，德国拜耳公司研制并生产牌号为Lewsti...
【技术保护点】
1.一种钯负载固体催化剂，其特征在于，包括：载体，所述载体为阳离子交换树脂，所述阳离子交换树脂的均一系数≤1.1；活性组分，所述活性组分为贵金属钯，所述贵金属钯以单质形态分布于所述载体内。
【技术特征摘要】
1.一种钯负载固体催化剂，其特征在于，包括：载体，所述载体为阳离子交换树脂，所述阳离子交换树脂的均一系数≤1.1；活性组分，所述活性组分为贵金属钯，所述贵金属钯以单质形态分布于所述载体内。2.如权利要求1所述的钯负载固体催化剂，其特征在于，所述阳离子交换树脂为耐130℃高温的阳离子交换树脂。3.一种权利要求1或2所述的钯负载固体催化剂的制备方法，其特征在于，包括如下步骤：采用阳离子交换树脂作为载体；采用氯化钯、硝酸钯或醋酸钯作为前体，配成浓度为0.1～10g/L的前体溶液；依次采用1％～10％盐酸溶液和超纯水以1～50BV/h速率在层析柱内对所述载体进行洗涤；将洗涤后的载体与所述前体溶液放入搅拌容器中，浸渍1～48h，浸渍温度为0～90℃；浸渍后，采用超纯水洗涤上述混合液；洗涤后，向洗涤后的混合液加入还原剂，还原3～24h；采用超纯水与氮气混合物在层析柱内洗涤还原后的混合液；采用1％～10％盐酸溶液和超纯水以1～50...
【专利技术属性】
技术研发人员：谈文姬，姜韶堃，何艳红，赵宁，宋春景，赵罗生，桂璐廷，陶志勇，
申请(专利权)人：上海核工程研究设计院有限公司，中国船舶重工集团公司第七一八研究所，
类型：发明
国别省市：上海,31