The invention discloses a medical air permeable, moisture permeable and degradable antimicrobial pressure sensitive adhesive, which is made from the following raw materials by weight percentage: dandelion extract, Eucommia ulmoides extract, modified organosilicon resin, hexamethylcyclotrisiloxane, Dodecylbenzene sulfonic acid solution, polyethyl silicate, sodium alginate, carob gum, polyoxyethylene/polycyanoethylene copolymer, sodium polyacrylate and purity. Water, isopropanol, octamethyltetrasiloxane, dodecyl polyoxyethylene ether, zinc cyclohexylthioacetate vanillate, citric acid, rhodium vinylsiloxane complex polysiloxane solution, methyl vinyl silicone oil, methyl hydrosiloxane oil. The pressure-sensitive adhesive disclosed by the invention has good biocompatibility, good adhesion performance, anti-bacterial, anti-mildew, small barrier effect, good air permeability and good moisture permeability, and is conducive to drug release, strong compliance, low cost, biodegradable, adaptable to the characteristics of soft and flexible skin surface and multiple wrinkles, and prolongs storage time.
【技术实现步骤摘要】
一种医用透气透湿可降解抗菌压敏胶黏剂
本专利技术涉及高分子材料
，特别涉及一种医用透气透湿可降解抗菌压敏胶黏剂。
技术介绍
胶黏剂在医疗卫生领域中的应用其实在很久以前就开始了,例如用于跌打损伤和内病外治的膏药（俗称狗皮膏药)在我国医学中数千年前就有了,随着医药科学的进步,胶黏剂在医疗领域的应用愈来愈多,例如橡皮膏、胶布牙齿、人工角膜、人造器官的生产及其与周围组织的粘接等。医疗卫生用胶黏剂应与人体组织适应,对人体无毒副作用或即使有副作用,其危害性也远小于其有益性,例如不能有异物反应、过敏反应、疼痛反应、炎症反应,粘接细胞组织的胶黏剂应对水有良好的湿润性,即具有一定的亲水性,另外要求使用方便,固化后胶层的机械性能,例如硬度、强度、弹性能与所粘接的组织相适应,易灭菌。经皮吸收制剂体系利用压敏胶系通过完整皮肤给药,使药物透过表皮由真皮内的毛细血管吸收进入全身循环,实现治疗或预防疾病的目的,又称经皮给药，从广义上来说,具有全身作用的凝胶剂、软膏剂、硬膏剂、贴剂、涂剂、涂膜剂等均或多或少利用压敏胶达到经皮给药的目的，尤其经皮贴剂,又称贴片为代表的使用压敏胶的药剂，在跌打...
【技术保护点】
1.一种医用透气透湿可降解抗菌压敏胶黏剂，其特征在于，由以下重量份的原料制得：蒲公英提取物21~33份、杜仲提取物17~23份、改性有机硅树脂51~73份、六甲基环三硅氧烷69~83份、十二烷基苯磺酸溶液（质量分数15%）50~63份、聚硅酸乙酯120~135份、海藻酸钠0.5~2.3份、角豆胶3.5~5.5份、聚氧乙烯/聚氰乙烯共聚物17~25份、聚丙烯酸钠13~21份、纯净水280~310份、异丙醇40~57份、八甲基四硅氧烷100~137份、十二烷基聚氧乙烯醚11~17份、环己基硫代醋香草酸锌0.6~1.3份、柠檬酸0.2~0.4份、铑‑乙烯基硅氧烷配合物的聚硅氧烷溶...
【技术特征摘要】
1.一种医用透气透湿可降解抗菌压敏胶黏剂，其特征在于，由以下重量份的原料制得：蒲公英提取物21~33份、杜仲提取物17~23份、改性有机硅树脂51~73份、六甲基环三硅氧烷69~83份、十二烷基苯磺酸溶液（质量分数15%）50~63份、聚硅酸乙酯120~135份、海藻酸钠0.5~2.3份、角豆胶3.5~5.5份、聚氧乙烯/聚氰乙烯共聚物17~25份、聚丙烯酸钠13~21份、纯净水280~310份、异丙醇40~57份、八甲基四硅氧烷100~137份、十二烷基聚氧乙烯醚11~17份、环己基硫代醋香草酸锌0.6~1.3份、柠檬酸0.2~0.4份、铑-乙烯基硅氧烷配合物的聚硅氧烷溶液(铑的质量分数为2.5×10-3)17~25份、甲基乙烯基硅油87~99份、甲基氢硅油13~21份。2.根据权利求1所述的一种医用透气透湿可降解抗菌压敏胶黏剂，其特征在于，所述甲基乙烯基硅油黏度(25℃)50~2000mPa·s,Si-Vi含量12%~15%(摩尔分数)，甲基氢硅油Si-H＜2个/mol,黏度(25℃)50~2000mPa·s。3.根据权利要求1所述的一种医用透气透湿可降解抗菌压敏胶黏剂，其特征在于，所述铑-乙烯基硅氧烷配合物的聚硅氧烷溶液的乙烯基硅氧烷为1，3二乙烯基四甲基二硅氧烷，质量分数为20~56%。4.根据权利要求1所述的一种医用透气透湿可降解抗菌压敏胶黏剂,其特征在于，所述改性有机硅树脂为丙烯酸改性有机硅,具体制法为在装有冷凝管、搅拌器的反应釜中加入100份当量纯净水,通氮气保护,恒温控制在85℃，室温下将28~41份六甲基三硅氧烷、3份乙烯基三甲氧基硅烷、3份乙烯基三乙氧基硅烷、1份乙烯基三异丙氧基硅烷、0.02~0.04份苯乙烯磺酸钠以及0.2份过硫酸铵在pH值为6~7的水溶液中均匀搅拌30min后,用氨水溶液中和，然后边搅拌边缓慢滴加至反应釜中,同时滴加甲基丙烯酸甲酯11~18份、苯乙烯5~15份、丙烯酸正丁酯48~50份、丙烯酸13~24份的混合溶液,滴加完毕后...
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。