The present invention relates to an anodizing solution for magnesium alloys, which is an aqueous solution containing silicate, fluorozirconate, complexing agent, regulator, sodium tripolyphosphate, auxiliaries and organic acids, and the organic acids are tannic acid and ascorbic acid. The addition of tannic acid and ascorbic acid in the anodizing solution can inhibit the violent reaction of magnesium alloy in the process of anodizing, so that the surface of magnesium alloy can obtain moderate depth, good homogeneity of pore, and is conducive to dyeing treatment in the later stage. The invention also provides a preparation method of magnesium alloy anodizing solution and an anodizing method of magnesium alloy.
【技术实现步骤摘要】
一种镁合金阳极氧化液及其制备方法及镁合金阳极氧化方法
本专利技术涉及一种镁合金阳极氧化液、制备方法及镁合金阳极氧化方法，属于材料表面处理
技术介绍
镁合金表面着色是目前研究的热点之一，其中阳极氧化后染色是较为热门的研究工艺。目前，铝合金在进行阳极氧化工艺后再采用着色方法，通常有二次着色法、电解着色法和多色作色法等，这些工艺已进入生产化阶段。镁合金的阳极氧化膜的构造与铝合金类似，也是由无孔的阻挡和多孔的表面层组成，不同之处在于铝合金阳极氧化表面孔洞细小，均匀，而镁合金的阳极氧化膜的孔隙与阻挡层的断裂和随后的氧化行为有关，表面层孔隙大且无规则，膜的孔隙率较高。镁合金阳极氧化所得到的膜层是不透明的，火花阳极氧化工艺，其孔隙率更大而且分布不均匀。许多用于铝合金阳极氧化着色反应的方法无法适用于镁合金的阳极氧化膜层的着色。由于镁本身的特性，工业化和生产远不及铝合金阳极氧化。现有技术中，生成的镁合金阳极氧化膜均匀性较差，且表面疏松粗糙，在外界压力下容易脱落；尤其是在染色后效果深浅不一。
技术实现思路
为解决上述问题，本专利技术提供了一种镁合金阳极氧化液，所述阳极氧化液为含...
【技术保护点】
1.一种镁合金阳极氧化液，其特征在于，所述阳极氧化液为含有硅酸盐、氟锆酸盐、络合剂、调节剂、三聚磷酸钠、助剂和有机酸的水溶液；所述有机酸为单宁酸和抗坏血酸。
【技术特征摘要】
1.一种镁合金阳极氧化液，其特征在于，所述阳极氧化液为含有硅酸盐、氟锆酸盐、络合剂、调节剂、三聚磷酸钠、助剂和有机酸的水溶液；所述有机酸为单宁酸和抗坏血酸。2.根据权利要求1所述的阳极氧化液，硅酸盐的含量为1-10g/L，氟锆酸盐为0.01-0.3g/L、络合剂为1-5g/L、调节剂为80-150g/L、三聚磷酸钠为1-10g/L、助剂为0.5-20g/L和有机酸为0.1-4g/L。3.根据权利要求1所述的阳极氧化液，所述有机酸中单宁酸和抗坏血酸的质量比为1：0.5-1.5。4.根据权利要求1所述的阳极氧化液，所述硅酸盐为硅酸钠和/或硅酸钾。5.根据权利要求1所述的阳极氧化液，所述氟锆酸盐为氟锆酸钾和/或氟锆酸钠。6.根据权利要求1所述的阳极氧化液，所述络合剂为二乙醇胺、三乙醇胺及乙二胺中的一种或一种以上。...
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。