The present invention relates to a method for preparing mesoporous carbon nitride and its products and applications. Nano-zinc oxide is used as precursor, nano-zinc oxide is first prepared into monodisperse nano-dispersion by grinding and dispersing, then the precursor of carbon nitride is fully mixed with zinc oxide dispersion and roasted, then the roasted product is fully stirred in hydrochloric acid, and finally prepared. To mesoporous carbon nitride. The mesoporous carbon nitride prepared by the method of the invention has small pore size and uniform size, simple operation, low difficulty, no use of dangerous hydrofluoric acid, and is suitable for large-scale popularization.
【技术实现步骤摘要】
介孔氮化碳的制备方法及其产品和应用
本专利技术属于纳米材料制备领域，具体涉及一种介孔氮化碳的制备方法及其产品和应用。
技术介绍
氮化碳是通过对含碳元素以及氮元素丰富的材料进行一定的焙烧合成的一种黄色纳米晶体。其晶体结构与石墨结构相似。因为氮化碳基团仅处于一个分子层内，因此只有微弱的范德华力可以将不同分子层之间连接起来。广为人知的是，光可以在这种材料中产生电子-空穴对。因此，氮化碳具备优异的光催化性能。其可以将低密度的太阳能转化为高密度的化学能或直接降解和矿化有机污染物，在解决能源短缺和环境污染等问题方面具有重要的应用前景。介孔氮化碳由于在氮化碳薄片上存在大量的2-50nm的小孔，使得其具有极高的比表面积、规则有序的孔道结构、狭窄的孔径分布等特点；相比较纯氮化碳来说，其具备优异的大分子的吸附、分离特点，可以在催化反应中发挥更大作用，提供更高的光催化效率。而且，这种有序孔道还可作为“微型反应器”，提高催化性能。目前介孔氮化碳的制备方式普遍采用纳米氧化硅用作模板，通过硬模板法制备介孔氮化碳，采用这种方式可以制备得到介孔氮化碳。但是这种方法有一些缺点，首先该法是先将氧化硅...
【技术保护点】
1.一种介孔氮化碳的制备方法，其特征在于，采用纳米氧化锌分散液作为前驱体、采用盐酸溶解掉模板的方式来制备介孔氮化碳的制备方法，包括如下步骤：1）纳米氧化锌分散液制备：按质量比为1:（0.05～0.6）：（1～100）精确称取纳米氧化锌、分散剂以及去离子水，首先将分散剂加入去离子水中，搅拌使其溶解后，再加入纳米氧化锌，搅拌混合均匀，然后研磨，得到单分散不团聚的纳米氧化锌分散液；2）在上述纳米氧化锌分散液中加入三聚氰胺，所述纳米氧化锌分散液与三聚氰胺的质量比为1:（0.01～0.5），然后在60～100℃下搅拌3h，将上述溶液蒸发干之后得到三聚氰胺与纳米氧化锌均匀混合物；将上述...
【技术特征摘要】
1.一种介孔氮化碳的制备方法，其特征在于，采用纳米氧化锌分散液作为前驱体、采用盐酸溶解掉模板的方式来制备介孔氮化碳的制备方法，包括如下步骤：1）纳米氧化锌分散液制备：按质量比为1:（0.05～0.6）：（1～100）精确称取纳米氧化锌、分散剂以及去离子水，首先将分散剂加入去离子水中，搅拌使其溶解后，再加入纳米氧化锌，搅拌混合均匀，然后研磨，得到单分散不团聚的纳米氧化锌分散液；2）在上述纳米氧化锌分散液中加入三聚氰胺，所述纳米氧化锌分散液与三聚氰胺的质量比为1:（0.01～0.5），然后在60～100℃下搅拌3h，将上述溶液蒸发干之后得到三聚氰胺与纳米氧化锌均匀混合物；将上述固体研磨之后放入坩埚中，以2.5℃/分钟的升温速率升温到400～600℃焙烧，保温1～5小时，得到棕黑色粉体；3）将上述焙烧得...
【专利技术属性】
技术研发人员：何丹农，徐少洪，王敬锋，林琳，陈超，金彩虹，
申请(专利权)人：上海纳米技术及应用国家工程研究中心有限公司，
类型：发明
国别省市：上海,31