The invention discloses a production and processing method for straight pipe of concrete pump truck boom bracket. Firstly, 45 # steel pipe is used as raw material, flange and bushing are processed well according to size requirements, both ends of straight pipe and flange are welded according to requirements, and the inner wall of formed boom bracket tube is quenched by high frequency, hardness of quenching layer is HRC55 60, depth of quenching layer is 1.0 2.0 mm; The hardness of quenching is HRC55 Under the same construction conditions, the service life of the boom pipe processed by the invention is 2_3 times longer than that of the ordinary boom pipe, and can reach 2.5_30,000 m 3.
【技术实现步骤摘要】
一种混凝土泵车臂架管直管生产加工方法
本专利技术涉及一种机械设备生产加工方法，具体是一种混凝土泵车臂架管直管生产加工方法。
技术介绍
因城市建设，以及各种工程建设的机械化施工的需要，用于混凝土输送的混凝土泵车已经成为混凝土机械化施工中的主要施工设备。混凝土泵车臂架管是输送混凝土的管道，由于直接和混凝土接触、摩擦，所以特别容易磨损、失效，成为混凝土泵车的主要易损件之一。现有的混凝土泵车臂架管一般采用20#无缝钢管，由于臂架管工作环境恶劣，长时间混凝土在臂架管内流动，对臂架管的耐磨性能有较高要求，然而由于原料本身耐磨性能较差，20#无缝钢管使用寿命一般为6-8千米3左右，寿命较短，增加了使用成本和混凝土施工作业的不连续性，影响了施工。为了提高臂架管的使用寿命，需要提高臂架管内壁的硬度以增加耐磨性，延长使用寿命。如此必须对内壁进行淬火处理，在现有条件下由于受泵车臂架重量的限制，臂架管在提高寿命的同时，要求不能增加重量，也就是不能增加壁厚。故怎样控制淬火时间、淬火温度、淬火层硬度、淬硬层硬度成为延长臂架管使用寿命的关键。
技术实现思路
本专利技术所要解决的技术问题是提供一种在...
【技术保护点】
1.一种混凝土泵车臂架管直管生产加工方法，其特征在于包括以下步骤：1）下料：以45# 钢管为原料，按尺寸要求下好直管，加工好法兰和衬套；2）将直管两端与法兰按要求焊接，成臂架管；3）对已成型臂架管的内壁进行高频淬火，淬火层硬度为HRC55‑60，淬火层深度为1.0‑2.0mm ；4）衬套整体淬火，淬火硬度为HRC55‑60 ；5）将衬套镶在两端的法兰内。
【技术特征摘要】
1.一种混凝土泵车臂架管直管生产加工方法，其特征在于包括以下步骤：1）下料：以45#钢管为原料，按尺寸要求下好直管，加工好法兰和衬套；2）将直管两端与法兰按要求焊接，成臂架管；3）对已成型臂架管的内壁进行高频淬火，淬火层硬度为HRC55-60，淬火层深度为1.0-2.0mm；4）衬套整体淬火，淬火硬度为HRC55-60；5）将衬套镶在两端的法兰内。2....
【专利技术属性】
技术研发人员：马安岭，
申请(专利权)人：安徽砀山金兄弟实业科技有限公司，
类型：发明
国别省市：安徽,34