一种用于乙炔法生产醋酸乙烯的催化剂及其制备方法技术

本发明专利技术提供一种用于乙炔法醋酸乙烯生产的催化剂及其制备方法。所述催化剂以有序介孔碳为载体，醋酸锌为活性组分。本发明专利技术使用的催化剂载体有序介孔碳具有有序介孔结构，能够有效减少积炭，延长催化剂的寿命，并且催化剂的比表面积高。在乙炔法制醋酸乙烯的反应中使用该催化剂能够显著提高醋酸的转化率，并且产物中醋酸乙烯的选择性高，时空收率也显著提高。

A Catalyst for the Production of Vinyl Acetate by Acetylene Method and Its Preparation Method

The invention provides a catalyst for ethylene acetate production by acetylene method and a preparation method thereof. The catalyst takes ordered mesoporous carbon as carrier and zinc acetate as active component. The ordered mesoporous carbon used in the catalyst carrier has ordered mesoporous structure, can effectively reduce coke deposition, prolong the life of the catalyst, and has high specific surface area of the catalyst. The use of the catalyst in the reaction of vinyl acetate with acetylene can significantly improve the conversion of acetic acid, and the selectivity of vinyl acetate in the product is high, and the space-time yield is also significantly improved.

【技术实现步骤摘要】
一种用于乙炔法生产醋酸乙烯的催化剂及其制备方法
本专利技术涉及催化剂制备
，具体涉及一种用于乙炔法合成醋酸乙烯的催化剂及制备方法。
技术介绍
醋酸乙烯，又称醋酸乙烯酯，是世界上产量最大的有机化工原料之一，也是醋酸主要的下游产品之一，工业用途广泛。可以通过自身聚合或与其他单体共聚生产许多化工产品。生产醋酸乙烯的方法有乙烯法和乙炔法。乙烯法制备醋酸乙烯使用贵金属催化剂，价格昂贵，并且乙烯的来源有限，因此，目前生产醋酸乙烯主要采用乙炔法。自1922年德国Muquaen成功开发出乙炔法气相合成醋酸乙烯以来，工业化装置中使用的一直是醋酸锌/活性炭催化剂。但是，醋酸锌/活性炭催化剂机械强度较差，并且作为载体的活性炭具有大量小于2nm的微孔，孔径较小，扩散阻力大，造成反应过程中中间产物不容易离开而产生结焦，堵塞其有效孔结构而造成催化剂活性下降，催化剂的使用寿命短，并且使用醋酸锌/活性炭催化剂副产物多，分离过程复杂。为了改善催化剂的性能，有采用超声、表面氧化处理等手段改善活性炭的孔结构及表面官能团来提高催化剂的活性；也有通过添加助剂的方式来提高催化剂活性；另外有尝试使用γ-氧化铝、高分子(树脂本文档来自技高网...

【技术保护点】
1.一种用于乙炔法生产醋酸乙烯的催化剂，所述催化剂以有序介孔碳为载体，以醋酸锌为活性组分。

【技术特征摘要】
2017.08.04 CN 20171065977871.一种用于乙炔法生产醋酸乙烯的催化剂，所述催化剂以有序介孔碳为载体，以醋酸锌为活性组分。2.根据权利要求1所述的催化剂，其特征在于，所述催化剂中醋酸锌与有序介孔碳的质量比为(0.1-0.6):1，优选为(0.30-0.56):1。3.根据权利要求1或2所述的催化剂，其特征在于，所述有序介孔碳的孔径为2-10nm，优选为3-10nm；和/或，孔容为0.3-1.4cm3/g，优选为0.4-1.2cm3/g；和/或，比表面积为350-1000m2/g，优选为500-900m2/g。4.一种根据权利要求1-3中任一项所述的催化剂的制备方法，其包括：步骤I：...

【专利技术属性】
技术研发人员：张敏华，陈爽，陈毅飞，汪宝和，董秀芹，姜浩锡，
申请(专利权)人：中国石油化工股份有限公司，
类型：发明
国别省市：北京,11