一种泡沫镍基Co-Mo-S双功能纳米复合材料及其制备方法和应用技术

本发明专利技术公开了一种泡沫镍基Co‑Mo‑S双功能纳米复合材料，包括作为基底的泡沫镍，所述泡沫镍上生长有Co9S8、CoMoS3.13和MoS2。泡沫镍在作为催化剂形成的载体的同时，在发生电催化反应过程中促进了电极与本申请之间的电子转移。MoS2、Co9S8和CoMoS3.13三相之间的协同作用，进一步提高了其催化性能。本申请同时具有优异HER和OER性能，且可在同一电解液中用作HER和OER催化剂。

Foamed nickel based Co-Mo-S bifunctional nanocomposite and preparation method and application thereof

The invention discloses a foamed nickel base Co Mo Mo S dual functional nano composite material, which comprises a foamed nickel as a base, and Co9S8, CoMoS3.13 and MoS2 on the foam nickel. Nickel foam acts as a catalyst carrier and promotes the electron transfer between the electrode and the application in the process of electrocatalytic reaction. The synergistic effect between MoS2, Co9S8 and CoMoS3.13 further improves the catalytic performance. This application has both excellent HER and OER properties and can be used as HER and OER catalysts in the same electrolyte.

【技术实现步骤摘要】
一种泡沫镍基Co-Mo-S双功能纳米复合材料及其制备方法和应用
本专利技术涉及电催化
，具体涉及一种泡沫镍基Co-Mo-S双功能纳米复合材料及其制备方法和应用。
技术介绍
随着化石燃料的短缺和世界人口不断增长，开发低成本、高效、清洁和可持续的能源转化和储存技术已经成为科学工作者的重要任务之一。氢气作为一种可储存、无污染、可再生的优质新能源得到了人们的广泛关注。其中，电催化析氢反应(HER)和析氧反应(OER)分解水制备氢气是一种高效、方便和有前景的方法。然而其缓慢的HER和OER动力学往往限制了体系的整体效率。目前，工业上普遍使用的HER电催化剂是铂基贵金属，而用于OER的催化剂为氧化铱和氧化钌，虽然催化活性较高，但是贵金属资源稀缺且成本较高等缺点极大限制了它们的工业化。因此，开发活性高、价格低廉且资源丰富的非贵金属电解水催化剂具有重要意义。近年来，人们致力于研究开发过渡金属硫化物、氮化物、磷化物和硒化物用作HER催化剂；过渡金属氧化物、氢氧化物和碳化物用作OER催化剂。然而，现有技术中同时具有优异HER和OER性能的电催化剂却鲜有报道。因此，如何制备一种可以在同一电解液中用作本文档来自技高网...

【技术保护点】
1.一种泡沫镍基Co‑Mo‑S双功能纳米复合材料，其特征在于，包括作为基底的泡沫镍，所述泡沫镍上生长有Co9S8、CoMoS3.13和MoS2。

【技术特征摘要】
1.一种泡沫镍基Co-Mo-S双功能纳米复合材料，其特征在于，包括作为基底的泡沫镍，所述泡沫镍上生长有Co9S8、CoMoS3.13和MoS2。2.一种制备泡沫镍基Co-Mo-S双功能纳米复合材料的方法，其特征在于，包括以下步骤：将碳酸钴粉末与硫代钼酸在水中并混合得到混合液，将泡沫镍浸泡于上述混合液中，在反应釜中加热至100～160℃反应3～8h后，得到泡沫镍基Co-Mo-S双功能纳米复合材料。3.如权利要求2所述的制备泡沫镍基Co-Mo-S双功能纳米复合材料的方法，其特征在于，所述碳酸钴与所述硫代钼酸铵质量比为0.5:1～1.5:1。4.如权利要求3所述的制备泡沫镍基Co-Mo-S双功能纳米复合材料的方法，其特征在于，所述碳酸钴粉末与硫代钼酸的质量比1:1。5.如权利要求2所述的制备泡沫镍基Co-Mo-S双功能纳米复合材料的方法，其特征在于，所述碳酸钴粉末通过以下...