一种钢包座砖填缝料及其制备方法技术

本发明专利技术公开了一种钢包座砖填缝料，原料由：刚玉、Al2O3粉、电熔镁砂、水泥、复合添加剂按重量份组成，所述Al2O3粉由a‑Al2O3粉和ρ‑Al2O3粉组成。本发明专利技术通过新设计的填缝料及施工，彻底解决了钢包串气现象，同时解决刚玉自流料不耐侵蚀，对座砖周围保护效果差的问题，提高了钢厂的生产效率，减少了劳动强度。

A kind of filling material for ladle block and its preparation method

The invention discloses a seam filling material for ladle block, which is composed of corundum, Al2O3 powder, fused magnesia, cement and composite additives according to weight. The Al2O3 powder is composed of a Al2O3 powder and P Al2O3 powder. Through the newly designed filling material and construction, the phenomenon of gas stringing in ladle is thoroughly solved, while the problem of corundum self-flowing material being not resistant to erosion and poor protection effect around the seating brick is solved, the production efficiency of the steel plant is improved, and the labor intensity is reduced.

【技术实现步骤摘要】
一种钢包座砖填缝料及其制备方法
本专利技术涉及一种钢包座砖填缝料及其制备方法，属于炼钢设备

技术介绍
目前，钢厂座砖周围大多使用刚玉自流料进行填缝，由于刚玉自流料经过高温烧结后，容易收缩产生缝隙，导致使用一段时间后，钢水容易渗透至填缝中，造成座砖周围起不到对座砖的保护作用，从而影响座砖使用寿命，造成串气现象，钢包被迫下线，影响生产。为了解决钢包座砖周围串气问题，需要开发一种高性能填缝料。
技术实现思路
本专利技术为解决上述问题，目的之一是：提供一种用于钢包座砖周围防串气填缝料；目的之二是提供该填缝料的制备方法。本专利技术为达到上述目的，所采取的技术方案是：一种钢包座砖填缝料，原料由：刚玉、Al2O3粉、电熔镁砂、水泥、复合添加剂按重量份组成，所述Al2O3粉由a-Al2O3粉和ρ-Al2O3粉组成。进一步的，所述a-Al2O3粉为500目a-Al2O3粉和1uma-Al2O3粉的混合物。进一步的，所述复合添加剂由硅微粉、高效复合减水剂、防爆纤维组成。进一步的，所述原料的重量比：刚玉75～80%、Al2O3粉10～14%、水泥3～7%，电熔镁砂3～7%，复合添加剂0.1～1%。更本文档来自技高网...

【技术保护点】
1.一种钢包座砖填缝料，其特征在于：原料由：刚玉、Al2O3粉、电熔镁砂、水泥、复合添加剂按重量份组成，所述Al2O3粉由a‑Al2O3粉和ρ‑Al2O3粉组成。

【技术特征摘要】
1.一种钢包座砖填缝料，其特征在于：原料由：刚玉、Al2O3粉、电熔镁砂、水泥、复合添加剂按重量份组成，所述Al2O3粉由a-Al2O3粉和ρ-Al2O3粉组成。2.根据权利要求1所述的钢包座砖填缝料，其特征在于：所述a-Al2O3粉为500目a-Al2O3粉和1uma-Al2O3粉的混合物。3.根据权利要求1所述的钢包座砖填缝料，其特征在于：所述复合添加剂由硅微粉、高效复合减水剂、防爆纤维组成。4.根据权利要求1所述的钢包座砖填缝料，其特征在于：所述原料的重量比：刚玉75～80%、Al2O3粉10～14%、水泥3～7%，电熔镁砂3～7%，复合添加剂0.1～1%。5.根据权利要求4所述的钢包座砖填缝料，其特征在于：所述复合添加剂由硅微粉55～70%、高效复合减水剂15～30%、防爆纤维10～20%组成。6.根据权利要求4所述的钢包座砖填缝料，其特征在于：所述刚玉由刚玉骨料和刚玉粉组成，其中刚...

【专利技术属性】
技术研发人员：李捷，金昭珍，常绍刚，朱广斌，李贺，
申请(专利权)人：安徽省萧县华龙耐火材料有限责任公司，
类型：发明
国别省市：安徽,34