The invention relates to a corundum dry ramming material for medium frequency induction furnace and a preparation method thereof. The technical scheme is as follows: using 48-68 wt% fused corundum particles, 20-40 wt% slab corundum and 6-16 wt% fused magnesia as raw materials, adding 0.5-1.5 wt% yttrium oxide powder, 0.5-1.0 wt% titanium dioxide powder, 0.5-2.0 wt% ZrOCl2.8H2O powder and 0.5-1.0 wt% nickel powder as raw materials, mixing evenly to produce corundum dry-type ramming furnace. Beat the material. The corundum dry ramming material for medium frequency induction furnace prepared by the invention has the characteristics of high fireproof, good volume stability, high temperature strength, good spalling resistance, excellent erosion resistance and good erosion resistance.
【技术实现步骤摘要】
一种中频感应炉用刚玉质干式捣打料及其制备方法
本专利技术属于中频感应炉用耐火材料领域。具体涉及一种中频感应炉用刚玉质干式捣打料及其制备方法。
技术介绍
随着经济的发展，中频感应炉冶炼已成为铸造、不锈钢冶炼及特种钢冶炼行业的主要冶炼设备之一。中频感应炉砌筑炉衬所用的干式捣打料是影响中频感应炉正常生产的重要材料。在使用过程中，干式捣打料的工作面需烧结形成具有强度较高的烧结层，有效抵抗钢水的冲刷和侵蚀；非工作面却应该保持未烧结的散状结构，且该结构应较厚，利于吸收热应力，达到阻止工作层裂纹的扩展及吸收裂纹的目的。目前，中频感应炉普遍使用刚玉-氧化镁质捣打料作炉衬。刚玉熔点高、热态体积稳定性好和具有优良的抗侵蚀性能，且利用刚玉和镁砂反应生成尖晶石产生的膨胀可以防止工作层因收缩导致的龟裂。然而，现有刚玉-镁质捣打料使用过程中工作层烧结强度较低，导致其抗冲刷性能和抗侵蚀性能较低；而工作面的烧结层较厚，非工作面散状结构较薄，不利于热应力的吸收，导致抗热震性能差和易于剥落，造成干式捣打料的快速损毁。
技术实现思路
本专利技术旨在克服现有技术缺陷，目的是提供一种耐火度高、体积稳定性好、高...
【技术保护点】
1.一种中频感应炉用刚玉质干式捣打料的制备方法，其特征在于：以48～68wt％的电熔刚玉颗粒、20～40wt％的板状刚玉和6～16wt％的电熔镁砂为原料，外加所述原料0.5～1.5wt％的氧化钇微粉、0.5～1.0wt％的二氧化钛细粉、0.5～2.0wt％的ZrOCl2·8H2O细粉和0.5～1.0wt％的氧化镍细粉，混合均匀，制得中频感应炉用刚玉质干式捣打料。
【技术特征摘要】
1.一种中频感应炉用刚玉质干式捣打料的制备方法，其特征在于：以48～68wt％的电熔刚玉颗粒、20～40wt％的板状刚玉和6～16wt％的电熔镁砂为原料，外加所述原料0.5～1.5wt％的氧化钇微粉、0.5～1.0wt％的二氧化钛细粉、0.5～2.0wt％的ZrOCl2·8H2O细粉和0.5～1.0wt％的氧化镍细粉，混合均匀，制得中频感应炉用刚玉质干式捣打料。2.根据权利要求1所述的中频感应炉用刚玉质干式捣打料的制备方法，其特征在于所述电熔刚玉颗粒的粒度为0.5～5mm；所述电熔刚玉颗粒的Al2O3含量＞99wt％。3.根据权利要求1所述的中频感应炉用刚玉质干式捣打料的制备方法，其特征在于所述板状刚玉的粒度为0.045～0.5mm；所述板状刚玉的Al2O3含量＞99.3wt％。4.根据权利要求1所述的中频感应炉用刚玉质干式捣打...