A processing method of aluminium alloy pre-stretching plate is introduced. When the plate is pre-stretched, the fixed length allowance is 60-100mm, and the bite length of each side of the stretching clamp is plate thickness + fixed length allowance. For plates with thickness less than 30 mm, the allowance of fixed length is 60-75 mm; for plates with thickness of 30-80 mm, the allowance of fixed length is 75-100 mm; for plates with thickness of 80-200 mm, the allowance of fixed length is 100 mm. The processing method of the aluminium alloy pre-stretching plate of the present invention solves the problem of large geometric waste, avoids the slippage of the stretching clamp and the tearing of the plate by flexibly selecting the length of the clamp, thus ensuring the quality of the aluminium alloy pre-stretching plate and improving the yield.
【技术实现步骤摘要】
一种铝合金预拉伸板加工方法
本专利技术涉及金属处理
,特别涉及铝合金预拉伸板的加工技术,填补了该领域国内外空白。
技术介绍
铝合金预拉伸板因其良好的强度与韧性被广泛应用于航空航天、兵器舰船、交通运输、机械制造、电子产品等国民经济领域,无论是出口还是内销均有着大量的需求。在铝合金厚板的生产过程中,由于淬火过程在板材中形成了大量的残余应力,因此在淬火后,要通过预拉伸过程来消除残余应力,同时满足客户对于板材平度等其他方面的需求。然而,在传统的拉伸作业中,对于不同厚度的铝合金预拉伸板钳口咬合长度的处理,一直都是固定每侧咬合300~400mm,有的企业规定咬合长度甚至达到500mm,生产一片拉伸板,几何废料占40%以上,造成产品几何废料大,成品率低的问题。
技术实现思路
为了在保证板材平度的基础上充分地消除板材的残余应力、提高产品成品率,本专利技术提供了一种铝合金预拉伸板加工方法。本专利技术为实现上述目的所采用的技术方案是:一种铝合金预拉伸板加工方法,板材预拉伸时,选取固定长度余量b为60~100mm,每侧拉伸钳口咬合长度L为板厚a+固定长度余量b。所述口咬合长度L,对于厚度小于30mm的板材,钳口咬合长度L选择固定长度余量b为60~75mm;对于厚度在30~80mm的板材,钳口咬合长度L选择固定长度余量b为75~100mm;对于厚度为80~200mm的板材,钳口咬合长度L选择固定长度余量b为100mm。本专利技术的铝合金预拉伸板加工方法,通过针对性的灵活选取钳口长度,既解决了几何废料大的问题,又避免了拉伸钳口滑脱及板材撕裂的问题,从而保证了铝合金预拉伸板的质量并 ...
【技术保护点】
1.一种铝合金预拉伸板加工方法,其特征在于:板材预拉伸时,选取固定长度余量(b)为60~100mm,每侧拉伸钳口咬合长度(L)为板厚(a)+固定长度余量(b)。
【技术特征摘要】
1.一种铝合金预拉伸板加工方法,其特征在于:板材预拉伸时,选取固定长度余量(b)为60~100mm,每侧拉伸钳口咬合长度(L)为板厚(a)+固定长度余量(b)。2.根据权利要求1所述的一种铝合金预拉伸板加工方法,其特征在于:所述钳口咬合长度(L),对于厚度...