The invention discloses a wrinkle-resistant shrinkage packaging film material, whose raw materials include polypropylene, ethylene-octene block copolymer, polyvinyl acetate, toughening nucleating agent, antioxidant and ultraviolet absorbent. Amino acid rare earth salt nucleating agent was prepared by the following process: adding aminopentanoic acid to maleic anhydride, heating melting reaction, vacuum drying, adding precursor to ethanol solvent, adding rare earth salt solution, heating stirring reaction, filtering and drying, to prepare amino acid rare earth salt nucleating agent. The packaging film material of the invention has good toughness, high strength and excellent wrinkle and shrinkage resistance.
【技术实现步骤摘要】
一种抗皱收缩包装膜材料
本专利技术涉及包装膜
,尤其涉及一种抗皱收缩包装膜材料。
技术介绍
塑料包装及塑料包装产品在市场上所占的份额越来越大,特别是复合塑料软包装,已经广泛地应用于食品、医药、化工等领域,其中又以食品包装所占比例最大,比如饮料包装、速冻食品包装、蒸煮食品包装、快餐食品包装等,这些产品都给人们生活带来了极大的便利。目前塑料包装膜主要包括:PVA涂布高阻隔薄膜、双向拉伸聚丙烯薄膜、低密度聚乙烯薄膜、聚酯薄膜、尼龙薄膜、流延聚丙烯薄膜、镀铝薄膜等七种。双向拉伸聚丙烯薄膜是由聚丙烯颗粒经共挤形成片材后,再经纵横两个方向的拉伸而制得的,具有物理稳定性、机械强度、气密性较好、透明度和光泽度较高、坚韧耐磨的特点,成本低,应用范围。但是双向拉伸聚丙烯薄膜的抗皱收缩性能差,限制其进一步发展与应用。
技术实现思路
基于
技术介绍
存在的技术问题,本专利技术提出了一种抗皱收缩包装膜材料,韧性好、强度高,抗皱收缩性能优异。本专利技术提出一种抗皱收缩包装膜材料,其原料按重量份包括:聚丙烯80-100份,乙烯-辛烯嵌段共聚物5-10份,聚醋酸乙烯酯1-5份,增韧成核剂0.5-2.5份,抗氧剂1-3份,紫外吸收剂0.5-2份。优选地,增韧成核剂原料按重量份包括:氨基酸类稀土盐成核剂50-70份,有机磷酸酯类成核剂30-50份。优选地,氨基酸类稀土盐成核剂采用如下工艺制备:将氨基戊酸加入马来酸酐,加热熔融反应后,真空干燥制得预制料;将预制料加入乙醇溶剂中,加入稀土盐溶液,加热搅拌反应,过滤,干燥,制得氨基酸类稀土盐成核剂。优选地,氨基戊酸、马来酸酐及稀土盐的摩尔比4-5:5 ...
【技术保护点】
1.一种抗皱收缩包装膜材料,其特征在于,其原料按重量份包括:聚丙烯80‑100份,乙烯‑辛烯嵌段共聚物5‑10份,聚醋酸乙烯酯1‑5份,增韧成核剂0.5‑2.5份,抗氧剂1‑3份,紫外吸收剂0.5‑2份。
【技术特征摘要】
1.一种抗皱收缩包装膜材料,其特征在于,其原料按重量份包括:聚丙烯80-100份,乙烯-辛烯嵌段共聚物5-10份,聚醋酸乙烯酯1-5份,增韧成核剂0.5-2.5份,抗氧剂1-3份,紫外吸收剂0.5-2份。2.根据权利要求1所述抗皱收缩包装膜材料,其特征在于,增韧成核剂原料按重量份包括:氨基酸类稀土盐成核剂50-70份,有机磷酸酯类成核剂30-50份。3.根据权利要求1所述抗皱收缩包装膜材料,其特征在于,氨基酸类稀土盐成核剂采用如下工艺制备:将氨基戊酸加入马来酸酐,加热熔融反应后,真空干燥制得预制料;将预制料加入乙醇溶剂中,加入稀土盐溶液,加热搅拌反应,过滤,干燥,制得氨基酸类稀...