The invention belongs to the field of titanium metallurgy, in particular to a method for preparing vanadium-containing sponge titanium. The technical problem to be solved by the present invention is to provide a method for preparing vanadium-containing sponge titanium, which includes the following steps: after distillation, refining and impurity removal of TiCl4 with high vanadium content without aluminium removal, it is directly introduced into the melting system of magnesium metal, and under the protection of inert gas, through the reduction of alkali metal and vacuum distillation process, vanadium-containing sponge titanium is prepared, which can be used as the raw material for preparing vanadium-containing titanium alloy. Material. The method of the invention can directly recover high-valent vanadium elements in TiCl4, simplify the refining process in the production process of TiCl4, provide special raw materials for vanadium-containing titanium alloys, and has important practical significance for the development of titanium alloys.
【技术实现步骤摘要】
制备含钒海绵钛的方法
本专利技术属于钛冶金领域，具体涉及一种制备含钒海绵钛的方法。
技术介绍
钛是轻质、高强、耐蚀、无毒的金属。工业纯钛不能热处理强化，其强度低而塑性好，主要用作耐蚀结构材料。钛合金由于合金元素的作用，而呈现多样化的特性，往往具有比纯钛更高的强度、耐热性和耐蚀性，在航空、航天、舰船、核能、军工等高科技领域，具有更广泛的用途。含钒钛合金由于钒的加入，既能提高钛合金强度又能改善性能。如用途最广的TC4钛合金，其中含有6％的Al和4％的V，可广泛应用于飞机结构中各种梁、隔框、滑轨、航空发动机的风扇等。钛及钛合金是由海绵钛加合金元素熔铸成钛锭，再经锻造、轧制、挤压等加工方法加工成材。含钒钛合金一般采用海绵钛和钒铝合金为原料，通过制备高纯的海绵钛、钒铝合金、适当添加铝豆，经过铸锭、加工成各种型材。实际在海绵钛制备过程中，其原料TiCl4经过氯化技术制备，传统工艺均采用92％以上钛渣氯化制得粗TiCl4，粗TiCl4采用精制除钒技术制得精TiCl4，通过镁热法蒸制得纯的海绵钛。后期在制备含钒钛合金时，确需要额外添加价值较贵的钒。同时后期在熔铸制锭过程中，钒元素...
【技术保护点】
1.制备含钒海绵钛的方法，其特征在于：包括以下步骤：含钒TiCl4先经蒸馏、精馏，再碱金属还原、真空蒸馏，制得含钒海绵钛。
【技术特征摘要】
1.制备含钒海绵钛的方法，其特征在于：包括以下步骤：含钒TiCl4先经蒸馏、精馏，再碱金属还原、真空蒸馏，制得含钒海绵钛。2.根据权利要求1所述的制备含钒海绵钛的方法，其特征在于：所述含钒TiCl4为含钒高炉渣经过高温碳化-低温氯化后的含钒TiCl4；或者含钒钛渣经过熔盐氯化或沸腾氯化后的TiCl4。3.根据权利要求2所述的制备含钒海绵钛的方法，其特征在于：所述含钒高炉渣经过高温碳化-低温氯化后的含钒TiCl4中VOCl3...
【专利技术属性】
技术研发人员：李开华，盛卓，李亮，苗庆东，
申请(专利权)人：攀钢集团攀枝花钢铁研究院有限公司，
类型：发明
国别省市：四川,51
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。