一种铁锈转化剂及其制备方法和应用技术

本发明专利技术提供了一种铁锈转化剂及其制备方法和应用，属于钢铁表面防腐涂装技术领域。本发明专利技术提供的铁锈转化剂由叔碳酸缩水甘油酯、没食子酸和十二烷基苯磺酸制备得到；所述叔碳酸缩水甘油酯、没食子酸和十二烷基苯磺酸的摩尔比为(1～8):1:(0.03～0.07)。本发明专利技术提供的铁锈转化剂制备原料简单，成本低，且可直接涂覆于锈蚀钢铁表面，无需进行任何预处理，转锈后锈层表面结构紧密，可以有效阻止锈蚀，且耐水性好。

A rust converter and its preparation method and Application

The invention provides a rust converting agent, a preparation method and application thereof, belonging to the technical field of anti-corrosion coating on steel surface. The rust converter provided by the invention is prepared from tertiary glycidyl carbonate, gallic acid and dodecylbenzenesulfonic acid, and the molar ratio of tertiary glycidyl carbonate, gallic acid and dodecylbenzenesulfonic acid is (1-8): 1:(0.03-0.07). The rust converting agent provided by the invention has the advantages of simple raw material preparation, low cost, and can be directly coated on the surface of rusted steel without any pretreatment. The rust layer has a compact surface structure after rusting, which can effectively prevent rust and has good water resistance.

【技术实现步骤摘要】
一种铁锈转化剂及其制备方法和应用
本专利技术涉及钢铁表面防腐涂装
，特别涉及一种铁锈转化剂及其制备方法和应用。
技术介绍
金属制件加工后在进行工装涂装前，需要经过传统的喷砂、打磨、人工除锈、酸洗等方法除去表面的锈和油，非常费时费力，同时在处理过程中会产生大量的污染物，污染环境。并且在经过一系列复杂的工序过后，有部分盲区锈蚀残留物无法除尽，将会直接影响后续的涂装质量。铁锈转化剂能够将铁锈转化为保护膜层，和传统方法相比，使用铁锈转化剂能够省去涂敷前的预处理工作，更加方便、环保。目前，铁锈转化剂主要有磷酸、单宁酸和亚铁氰化钾等。磷酸型铁锈转化剂耐水性较差；单宁酸与铁锈反应后，生成单宁酸铁络合物，可以很好地附着在钢铁表面上，但只能在锈层十分均匀的条件下使用，在锈层不均匀的条件下除锈效果较差；亚铁氰化钾与铁锈作用后可生成蓝色的亚铁氰酸盐(即普鲁士蓝)，是一种具有较强遮盖力的颜料，但直接使用效果很差，一般只能用于喷砂后对局部未除尽的残锈作辅助处理。
技术实现思路
有鉴于此，本专利技术目的在于提供一种铁锈转化剂及其制备方法和应用。本专利技术提供的铁锈转化剂耐水性好、除锈效果好，且可直接应用于锈蚀本文档来自技高网...

【技术保护点】
1.一种铁锈转化剂，其特征在于，由叔碳酸缩水甘油酯、没食子酸和十二烷基苯磺酸制备得到；所述叔碳酸缩水甘油酯、没食子酸和十二烷基苯磺酸的摩尔比为(1～8):1:(0.03～0.07)。

【技术特征摘要】
1.一种铁锈转化剂，其特征在于，由叔碳酸缩水甘油酯、没食子酸和十二烷基苯磺酸制备得到；所述叔碳酸缩水甘油酯、没食子酸和十二烷基苯磺酸的摩尔比为(1～8):1:(0.03～0.07)。2.根据权利要求1所述的铁锈转化剂，其特征在于，所述叔碳酸缩水甘油酯、没食子酸和十二烷基苯磺酸的摩尔比为(2～6):1:(0.04～0.05)。3.权利要求1或2所述铁锈转化剂的制备方法，包括以下步骤：将叔碳酸缩水甘油酯、没食子酸和十二烷基苯磺酸混合，使叔碳酸缩水甘油酯和没食子酸进行环氧开环酯化反应，得到铁锈转化剂。...

【专利技术属性】
技术研发人员：何文诗，曾显华，幸芦笙，
申请(专利权)人：五邑大学，
类型：发明
国别省市：广东,44