The invention discloses a special rubber powder for reducing friction and noise, which belongs to the technical field of friction materials. Rubber powder specially used for friction materials is composed of the following substances by weight: styrene-butadiene rubber 10 30 parts, sulfur 5 20 parts, accelerator 2 15 parts, magnesium oxide 2 10 parts, nanometer heavy calcium 15 40 parts, cotton fiber 5 20 parts, composite mineral fiber 1 10 parts. The preparation methods are as follows: (1) weighing and proportioning according to the proportion, mixing evenly; (2) mixing the mixture in the middle; (3) mixing the material in the middle through the open mill, granulating through the crusher, then sieving through the sieve machine, and finally packaging. The preparation method of the rubber powder for reducing wear and noise is simple, the performance of reducing wear and noise is superior, and the temperature resistance is improved.
【技术实现步骤摘要】
一种摩擦材料专用减磨减噪橡胶粉及其制备方法
本专利技术涉及摩擦材料
技术介绍
随着现代生活节奏的加快和生活水平的提高，家庭轿车已经越来越普遍，同时人们对汽车的制动效果也越来越看重。汽车在多种路况下的安全性和驾驶舒适性直接考验汽车制动性能，这就要求汽车的刹车片在高速高温制动条件下性能稳定、噪音低，而刹车片性能的直接影响因素就是生产刹车片的摩擦材料，在摩擦材料中橡胶粉的性能又起到决定作用。现有摩擦材料常用的橡胶粉为淡黄色丁腈橡胶粉，虽能增加产品的弹性，但是减磨减噪性能较差，成本高。
技术实现思路
本专利技术要解决的技术问题是提供一种摩擦材料专用减磨减噪橡胶粉及其制备方法，制备方法简单，减磨减噪性能优越，耐温性能提高。为解决上述技术问题，本专利技术所采取的技术方案是：一种摩擦材料专用减磨减噪橡胶粉，原料按重量份包括以下物质：丁苯橡胶10-30份、硫磺5-20份、促进剂2-15份、氧化镁2-10份、纳米级重钙15-40份、棉纤维5-20份、复合矿物纤维1-10份。优选的原料按重量份包括以下物质：丁苯橡胶15-20份、硫磺8-15份、促进剂5-10份、氧化镁5-8份、...
【技术保护点】
1.一种摩擦材料专用减磨减噪橡胶粉，其特征在于：原料按重量份包括以下物质：丁苯橡胶10‑30份、硫磺 5‑20份、促进剂2‑15份、氧化镁2‑10份、纳米级重钙15‑40份、棉纤维5‑20份、复合矿物纤维1‑10份。
【技术特征摘要】
1.一种摩擦材料专用减磨减噪橡胶粉，其特征在于：原料按重量份包括以下物质：丁苯橡胶10-30份、硫磺5-20份、促进剂2-15份、氧化镁2-10份、纳米级重钙15-40份、棉纤维5-20份、复合矿物纤维1-10份。2.根据权利要求1所述的减磨减噪橡胶粉，其特征在于：原料按重量份包括以下物质：丁苯橡胶15-20份、硫磺8-15份、促进剂5-10份、氧化镁5-8份、纳米级重钙20-30份、棉纤维8-10份、复合矿物纤维3-7份。3.根据权利要求2所述的减磨减噪橡胶粉，其特征在于：原料按重量份包括以下物质：丁苯橡胶18份、硫磺10份、促进剂8份、氧化镁7份、纳米级重钙25份、棉纤维9份、复合矿物纤维5份。4.根据权利要...