The invention provides a preparation method of polyvinyl chloride kitchen and toilet panels, which comprises the following steps: the materials are put into the hot mixing pan in the order of recycled materials, plasticizer, polyvinyl chloride resin, heavy calcium regulator, recycled materials, and the remaining small materials are added after stirring for 30 to 40 minutes to 100 degrees Celsius, mixing for 10 to 12 minutes to 120 degrees Celsius, and cooling for 3 to 5 minutes. The cooling material is then conveyed to the extruder, which is heated by the barrel screw to make it well plasticized and conveyed to the die. Temperature and pressure in the die are controlled to extrude. The final product is obtained by cooling and pressing on the setting table, and the tractor is moved out. It has the advantages of low density, high hardness, high nail holding force and low water absorption.
【技术实现步骤摘要】
一种聚氯乙烯厨卫板的制备方法
本专利技术涉及一种聚氯乙烯厨卫板的制备方法，属于聚氯乙烯板材
技术介绍
近年来，随着经济的发展，政府对环境也越来越重视。国家大力提倡开发节能、绿色产品，PVC是一种节能型环保产品。因此，推广应用PVC产品是节约资源、节约能耗、“以塑代木”、“以塑代钢”的重要措施。其中，PVC板由于具有可锯、可钉、可刨、可粘等加工性能，并且具有防水、防火、防虫蛀、耐碱、防腐、隔音、有较好的稳定性和耐候性等特点，得到了很好的发展，广泛应用于家具板、建筑板、广告板等。对于PVC厨卫板，生产中的难题是密度做不下来，板材发脆易断裂，表面硬度低，吸水率过高，握钉力低，且生产成本较高生产不稳定。生产配方和工艺设定也是随着生产不断更改调试，做不到大规模稳定统一生产，现有配方组成较为复杂。
技术实现思路
本专利技术的目的在于提供一种聚氯乙烯厨卫板的制备方法，具有密度低、硬度大、握钉力高、吸水率低的优点。所述的聚氯乙烯厨卫板的制备方法，包括以下步骤：将物料按照回收料-增塑剂-聚氯乙烯树脂-重钙-调节剂-聚氯乙烯树脂-重钙-回收料的顺序依次投入热混锅，搅拌升温30-...
【技术保护点】
1.一种聚氯乙烯厨卫板的制备方法，其特征在于包括以下步骤：将物料按照回收料‑增塑剂‑聚氯乙烯树脂‑重钙‑调节剂‑聚氯乙烯树脂‑重钙‑回收料的顺序依次投入热混锅，搅拌升温30‑40min至温度为100℃后加入剩余小料，10‑12min搅拌升温至120℃后，3‑5min降温至60‑70℃，10‑20min降温至40‑50℃，然后将冷却物料输送至挤出机，经料筒螺杆加热使其塑化良好输送至模具，控制模具内温度压力挤出，经由定型台冷却压合定性，牵引机迁出得到成品。
【技术特征摘要】
1.一种聚氯乙烯厨卫板的制备方法，其特征在于包括以下步骤：将物料按照回收料-增塑剂-聚氯乙烯树脂-重钙-调节剂-聚氯乙烯树脂-重钙-回收料的顺序依次投入热混锅，搅拌升温30-40min至温度为100℃后加入剩余小料，10-12min搅拌升温至120℃后，3-5min降温至60-...