A method for preparing hemihydrate gypsum fiber from desulfurized gypsum includes the following steps: drying desulfurized gypsum to remove free water; screening desulfurized gypsum after drying to remove large impurities in it; adding desulfurized gypsum after screening to hydrochloric acid containing magnesium chloride crystallizer, reacting at a certain temperature for a period of time, and then draining with the existing desulfurized gypsum; Machine solvents are used to wash the filtered cake, and drying the filtered cake to obtain hemihydrate gypsum fibers. The length-diameter ratio of hemihydrate gypsum fibers prepared by the method in this application is 400, which simplifies the preparation process, reduces energy consumption and realizes the recycling and reuse of industrial solid waste desulfurization gypsum.
【技术实现步骤摘要】
一种由脱硫石膏制备半水石膏纤维的方法
本申请涉及但不限于无机化学材料制备领域，特别涉及但不限于一种由脱硫石膏制备半水石膏纤维的方法。
技术介绍
半水石膏纤维是半水硫酸钙的纤维状单晶体，是一种新型的具有很高综合性能的无机材料。半水石膏纤维集增强纤维和超细无机填料二者的优势于一体，可作为补强增韧剂或功能型填料用于塑料、橡胶、涂料、油漆、造纸、沥青、摩擦和密封材料、包覆电线的高绝缘材料中。目前石膏纤维的制备方法主要是水热法，水热反应的温度一般为105-150℃或更高，压力为200-500Kpa，过滤的方式一般为压滤，压滤时，温度一般不低于100℃，制备出的石膏纤维长径比一般为50-200。该法对工艺要求较高，能耗较大。
技术实现思路
以下是对本文详细描述的主题的概述。本概述并非是为了限制权利要求的保护范围。本申请提供了一种工艺条件温和、能耗较低的利用脱硫石膏制备半水石膏纤维的方法。具体地，本申请提供了一种由脱硫石膏制备半水石膏纤维的方法。本申请所提供的由脱硫石膏制备半水石膏纤维的方法，包括以下步骤：干燥：将脱硫石膏进行干燥，除去其中的游离水；筛分：将干燥后的脱硫石膏进行筛分...
【技术保护点】
1.一种由脱硫石膏制备半水石膏纤维的方法，所述方法包括以下步骤：干燥：将脱硫石膏进行干燥，除去其中的游离水；筛分：将干燥后的脱硫石膏进行筛分，除去其中的大颗粒杂质；常压水热反应：将筛分后的脱硫石膏加入含有氯化镁转晶剂的盐酸中，在一定温度下反应一段时间后抽滤；洗涤：用有机溶剂对抽滤后得到的滤饼进行洗涤；干燥：将洗涤后的滤饼烘干，即得到半水石膏纤维。
【技术特征摘要】
1.一种由脱硫石膏制备半水石膏纤维的方法，所述方法包括以下步骤：干燥：将脱硫石膏进行干燥，除去其中的游离水；筛分：将干燥后的脱硫石膏进行筛分，除去其中的大颗粒杂质；常压水热反应：将筛分后的脱硫石膏加入含有氯化镁转晶剂的盐酸中，在一定温度下反应一段时间后抽滤；洗涤：用有机溶剂对抽滤后得到的滤饼进行洗涤；干燥：将洗涤后的滤饼烘干，即得到半水石膏纤维。2.根据权利要求1所述的方法，其中，所述将脱硫石膏进行干燥为将脱硫石膏在40-50℃下干燥4-6h。3.根据权利要求1所述的方法，其中，所述筛分为过100-...
【专利技术属性】
技术研发人员：张晓菲，陈红霞，李帆，王霞，冉秀云，
申请(专利权)人：北新集团建材股份有限公司，
类型：发明
国别省市：北京,11