The invention discloses a pre-dispersed masterbatch without nitrosamine, which belongs to the technical field of rubber additives. The pre-dispersed masterbatch is made of the following components: mixed accelerator 72.0-82.0 phr, rubber carrier 6.0-10.0 phr, processing oil 0-20.0 phr and processing assistant 0-8.0 phr, which is a mixture of zinc dibenzyl dithiocarbamate and N tert-butyl-2 benzothiazole sulfosulfonamide in a ratio of 2-5:1. The invention can effectively improve the vulcanization rate, shorten the vulcanization time, have good scorching safety, and do not produce nitrosamines. It has good compatibility with rubber, good dispersion, easy mixing of rubber, and can effectively enhance physical properties such as tensile strength, tear strength, etc.
【技术实现步骤摘要】
一种无亚硝胺产生的预分散母胶粒
本专利技术涉及橡胶助剂
，具体涉及一种无亚硝胺产生的预分散母胶粒。
技术介绍
在橡胶的硫化成型过程中，除了要加入硫化剂、硫化促进剂、防焦剂外，为提高硫化速度，一般还需要加入硫化活性剂，硫化活性剂具有活化硫化体系、提高硫化橡胶的交联密度、提高硫化胶的耐老化性能等作用。在橡胶的高温硫化过程中，硫化促进剂会在硫化过程中产生仲胺，与空气中或添加剂中的氮氧化物在一定条件下会生成稳定的亚硝胺，并且亚硝胺很难通过洗涤、浸泡去除掉，在使用过程可能会释放出致癌物质亚硝胺，严重威胁着人类的健康。二硫代氨基甲酸锌(ZDMC)在橡胶工业中应用广泛，使用量十分大，其具有硫化速度快、不污染不着色、工艺成熟的优点，但却容易在硫化过程中产生对人体有害且难以除去的亚硝胺。因此，开发硫化时间短、焦烧安全性好、不产生亚硝胺的预分散母胶粒配方体系，符合市场销售或使用需求，将是扩展橡胶应用发展的重要研究课题之一。
技术实现思路
为了克服现有技术的不足，本专利技术的目的在于提供一种硫化时间短、焦烧安全性好、不产生亚硝胺的预分散母胶粒的配方。为解决上述问题，本专利技术所采用的...
【技术保护点】
1.一种无亚硝胺产生的预分散母胶粒，其特征在于：包括以下组分：混合促进剂72.0～82.0％； 橡胶载体6.0～10.0％；加工油0～20.0％； 加工助剂0～8.0％；其中，所述混合促进剂是由二苄基二硫代氨基甲酸锌与N‑叔丁基‑2‑苯並噻唑次磺酰胺按2～5:1的比例混合得到的混合物。
【技术特征摘要】
1.一种无亚硝胺产生的预分散母胶粒，其特征在于：包括以下组分：混合促进剂72.0～82.0％；橡胶载体6.0～10.0％；加工油0～20.0％；加工助剂0～8.0％；其中，所述混合促进剂是由二苄基二硫代氨基甲酸锌与N-叔丁基-2-苯並噻唑次磺酰胺按2～5:1的比例混合得到的混合物。2.根据权利要求1所述的无亚硝胺产生的预分散母胶粒，其特征在于：包括以下组分：混合促进剂80.0％、橡胶载体8.0％、加工油11.0％、加工助剂1.0％。3.根据权利要求1所述的无亚硝胺产生的预分散母胶粒，其特征在于：包括以下组分：混合促进剂75.0％、橡胶载体10％、加工油...
【专利技术属性】
技术研发人员：甘仲豪，
申请(专利权)人：珠海科茂威新材料有限公司，
类型：发明
国别省市：广东,44