The invention relates to a method for preparing high molecular weight polylactic acid by twin-screw extruder, which uses twin-screw extruder as reaction vessel to prepare polylactic acid. The raw material components and weight components are as follows: 100 parts of lactide; 0.2 0.4 parts of antioxidant; 0.1 0.3 parts of catalyst; 0.1 0.3 parts of lubricant. The invention improves the traditional synthesis method of polylactic acid, realizes ring-opening polymerization of lactide to prepare polylactic acid in a twin-screw extruder. The method solves the problems of low molecular weight and non-continuous production; the production equipment and process are simple, the reaction speed is fast, the production efficiency is high, and the synthesis process is more stable and reliable.
【技术实现步骤摘要】
一种通过双螺杆挤出机制备高分子量聚乳酸的方法
本专利技术涉及一种通过双螺杆挤出机制备高分子量聚乳酸的方法，属高分子材料制造领域。
技术介绍
聚乳酸（PLA）是一种新型环保的热塑性聚合物，其优点是具有良好的生物相容性和生物降解性。因其具有无毒、降解产物可参与人体新陈代谢等有点，被美国食品药品管理局批准，可广泛用于缓释胶囊、手术缝合线、骨科固定材料以及作为通用高分子材料等使用。聚乳酸（PLA）的合成方法主要有乳酸直接缩聚法和丙交酯开环聚合法。目前采用较多的是丙交酯开环聚合法，例如专利文献WO90/01521介绍了由丙交酯开环聚合生产聚乳酸的过程。虽然可以获得分子量较高的聚乳酸产物，但反应时间往往要在24小时以上，特别是丙交酯精制中需要多次提纯于重结晶，生产效率低下带来的成本问题很大程度的限制了聚乳酸产品大规模生产；乳酸直接缩聚法的主要缺点是水作为副产物难以从体系中排除，阻碍了反应向生成聚合物的方向进行，较难得倒高分子量的聚合产物。采用双螺杆挤出反应法通过丙交酯开环制备聚乳酸，不仅生产设备简单，而且无需进行多次提纯与重结晶，大大简化生产工艺流程，提高生产效率，同时也避免...
【技术保护点】
1.一种通过双螺杆挤出机制备高分子量聚乳酸的方法，其特征在于所述的聚乳酸材料包括如下按重量份计算的组成：丙交酯100份；抗氧剂0.2‑0.4份；催化剂0.1‑0.3份；润滑剂0.1‑0.3份。
【技术特征摘要】
1.一种通过双螺杆挤出机制备高分子量聚乳酸的方法，其特征在于所述的聚乳酸材料包括如下按重量份计算的组成：丙交酯100份；抗氧剂0.2-0.4份；催化剂0.1-0.3份；润滑剂0.1-0.3份。2.根据权力要求1中所述的一种高分子量聚乳酸材料及其制备方法，其特征在于所述的丙交酯为自制L-丙交酯。3.根据权利要求1中所述的一种高分子量聚乳酸材料及其制备方法，其特征在于所述的抗氧剂为抗氧剂1010，抗氧剂168，抗氧剂626和抗氧剂1098中的一种或几种。4.根据权利要求1中所述的一种高分子量聚乳酸材料及其制备方法，其特征在于所述的催化剂为辛酸亚锡，氧化锌中，氯化亚锡的一种。5.根据权利要求1中所述的一种高分子量聚乳酸材料及其制备方法，其特征在于所述的润滑剂为硬脂酸，甘油，石蜡，环...
【专利技术属性】
技术研发人员：赫凯，敖广宇，
申请(专利权)人：沈阳中博环保科技研发有限公司，
类型：发明
国别省市：辽宁,21