The invention discloses a high aluminium glass capable of rapid ion exchange, which contains 55-65% SiO 2, 315-19% AlO 2, 3-10% NaO 2, B2O 31.5-5%, P2O 54-10%, LiO 4-7%, MgO 3-7%, SnO 2 0-0.5% and the remainder KO 2. The invention improves the intrinsic strength of glass by increasing the content of Al2O3 in glass, and further improves the chemical toughening and melting properties of glass by reasonably adjusting the content of Li2O and P2O5 in glass, so that it can obtain higher surface stress and deeper stress layer in a relatively short time. At the same time, the glass surface can have double stress layer by chemical strengthening. Used as protective glass for touch screen electronic products such as mobile phones.
【技术实现步骤摘要】
一种可快速离子交换的高铝玻璃
本专利技术属于玻璃材料
，具体涉及一种可快速离子交换的高铝玻璃。
技术介绍
随着智能手机屏幕的不断增大，玻璃成为整机结构设计中重要的一部分。而在整机破坏实验中，整机跌落测试常出现玻璃破裂的情况，究其原因，微裂纹的存在对玻璃实际强度影响最大。为了阻止微裂纹的扩展，提高玻璃的强度，化学增强法是目前业界熟知的一种技术。目前，玻璃的发展以促进玻璃的离子交换能力为主要发展方向。当玻璃进行离子交换时，玻璃的离子交换效果取决于离子交换的温度和时间，温度越高，离子交换的速度越快，压应力层越深，但表面压缩应力值越小，这主要是由于离子交换过程中玻璃存在应力松弛的现象。一般可通过降低离子交换的温度减轻玻璃的应力松弛，从而维持较高的表面压缩应力值，但同时会造成离子交换的效率降低，导致压缩应力层过低，因此是不可取的。基于此，本专利技术提供了一种高铝含量的化学强化玻璃，其通过Li离子与Na离子交换达到较高的DOL（应力层深度），并通过Na离子与K离子交换达到较高的CS（表面压应力）。
技术实现思路
本专利技术的目的在于提供一种可快速离子交换的高铝玻璃，其具有较...
【技术保护点】
1. 一种高铝玻璃，其特征在于：按摩尔百分数计，其所含化学成分包括：SiO2 55~65%、Al2O3 15~19%、Na2O 3~10%、P2O5 4~10%、Li2O 4~7%。
【技术特征摘要】
1.一种高铝玻璃，其特征在于：按摩尔百分数计，其所含化学成分包括：SiO255~65%、Al2O315~19%、Na2O3~10%、P2O54~10%、Li2O4~7%。2.一种高铝玻璃，其特征在于：按摩尔百分数计，其所含化学成分为：SiO255~65%、Al2O315~19%、Na2O3~10%、B2O31.5~5%、P2O54~10%、Li2O4~7%、MgO3~7%、SnO20~0.5%，余量为K2O。3.根据权利要求1或2所述的高铝玻璃，其特征在于：所述高铝玻璃在380℃~430℃条件下、于硝酸钾盐浴中进行两次...
【专利技术属性】
技术研发人员：陈招娣，梁新辉，林威廷，洪立昕，
申请(专利权)人：科立视材料科技有限公司，
类型：发明
国别省市：福建,35