The invention discloses a preparation method of a volatile organic acid gas sensor. The method uses quartz crystal oscillator plate coated with gold electrode as the base and drip coating to coat poly (1 vinyl 3 butyl imidazolium bromide) solution on the surface of quartz crystal oscillator electrode. The polymer film is dried and formed as a gas sensitive film on the surface of quartz crystal oscillator plate, and a gas sensor is composed with the base. The gas sensor of the invention has high selectivity and sensitivity to organic acid gas, simple preparation method, low cost and large-scale application prospect.
【技术实现步骤摘要】
挥发性有机酸性气体传感器的制备方法
本专利技术涉及一种挥发性有机酸性气体传感器的制备方法，属于气体传感
技术介绍
气体传感器在医药、能源、环境等众多领域有着广泛应用，尤其是对有毒有害气体的监测。挥发性有机酸(如乙酸)是重要的工业原料，但其挥发气体具有腐蚀性，会对人体造成伤害，对其进行有效的监测十分必要。石英晶体微天平(QCM)是一种极其灵敏的质量检测仪器，可以检测纳克级的质量变化，其具有稳定性好，灵敏的高，操作便捷等优点，常用于监测外界环境的微小变化。通过在石英晶振片表面沉积敏感薄膜，QCM可实现对不同气体的检测，其质量变化取决于气体分子与敏感薄膜的相互作用，因此选择合适的敏感薄膜是提高QCM传感器性能的关键。聚合物由于其易于沉积且具有成本优势成为被研究最多的一类敏感材料。《SyntheticMetals,1997,87,201-204》报道了采用聚邻茴香胺为敏感薄膜的QCM传感器，虽然通过增加膜厚可增强灵敏度，但对乙酸的最小检测浓度为1.84μg/ml，无法进行低浓度的乙酸检测。《SensorsandActuatorsB,2009,137,741–74...
【技术保护点】
1.挥发性有机酸性气体传感器的制备方法，其特征在于，具体步骤如下：将0.1～0.2mg/ml的聚合离子液体聚(1‑乙烯基‑3‑丁基咪唑溴盐)溶液滴涂到洁净的AT切型的石英晶振片金电极表面，干燥，得到挥发性有机酸性气体传感器。
【技术特征摘要】
1.挥发性有机酸性气体传感器的制备方法，其特征在于，具体步骤如下：将0.1～0.2mg/ml的聚合离子液体聚(1-乙烯基-3-丁基咪唑溴盐)溶液滴涂到洁净的AT切型的石英晶振片金电极表面，干燥，得到挥发性有机酸性气体传感器。2.根据权利要求1所述的制备方法，其特征在于，所述的AT切型的石英晶振片使用前用食人鱼溶液清洗金电极表面杂质并用水洗净，氮气吹干。3...
【专利技术属性】
技术研发人员：乔旭，张业浩，吉庆敏，
申请(专利权)人：南京理工大学，
类型：发明
国别省市：江苏,32