The invention provides a high barrier PVA-based composite film, which is weighed by weight as follows: corn starch 20 30, PVA40 50, Modified Hydrotalcite 10 20, keratin solution 30 50, sodium carboxymethyl cellulose 10 20, polyethylene glycol 5 15, crosslinking agent 3 10, plasticizer 3 10, water 100 150. The Modified Hydrotalcite layer in the invention has a high degree of encapsulation of the matrix molecular chain, which makes it difficult for the polyvinyl alcohol molecular chain to diffuse into water and plays a role of fixing the matrix, while the interaction of various matrix materials also prevents the diffusion of water molecules, and the mechanical properties of the composite materials are maintained at a higher level.
【技术实现步骤摘要】
一种高阻隔性PVA基复合膜及其制备方法
本专利技术涉及包装膜材料，具体涉及一种高阻隔性PVA基复合膜及其制备方法。
技术介绍
食品包装是现代食品生产的最后一个环节，不仅要方便储存和运输，而且应能保护食品质量和卫生，从而延长货架期和提高商品价值。随着人们环保意识的加强，越来越多的人们开始关注绿色环保，对食品包装材料要求绿色包装。绿色包装又可以称为无公害包装和环境之友包装，指对生态环境和人类健康无害，能重复使用和再生，符合可持续发展的包装。聚乙烯醇(PVA)是一种分子主链为碳链、侧链含有大量羟基的亲水性聚合物，具有良好的成膜性。由PVA制得的薄膜具有无毒无味、透明度高、气体阻隔性好、不吸灰尘和力学性能良好等特点，尤其是它可完全生物降解，符合绿色环保的发展要求，因此在包装、分离纯化和生物医学等领域有良好的应用前景。尽管PVA薄膜在干燥状态下具有良好的力学性能和气体阻隔性，但当其处于潮湿或水环境中时，就会吸水发生溶胀甚至溶解，膜的这些性能出现明显下降。
技术实现思路
要解决的技术问题：本专利技术的目的是提供高阻隔性PVA基复合膜，具有良好阻隔性的基础上，耐水性得到很好的提高。...
【技术保护点】
1.一种高阻隔性PVA基复合膜，其特征在于，按重量份称取以下成分：玉米淀粉20‑30份、PVA40‑50份、改性水滑石10‑20份，角蛋白溶液30‑50份，羧甲基纤维素钠10‑20份，聚乙二醇5‑15份，交联剂3‑10份，增塑剂3‑10份，水100‑150份；其中水滑石的改性方法为：将水滑石加入浓度50%的乙醇水溶液中，加热至60℃，恒温搅拌2h，然后加入月桂醇醚磷酸酯钾盐，调节pH至4，在60℃下反应4h，过滤洗涤烘干即可。
【技术特征摘要】
1.一种高阻隔性PVA基复合膜，其特征在于，按重量份称取以下成分：玉米淀粉20-30份、PVA40-50份、改性水滑石10-20份，角蛋白溶液30-50份，羧甲基纤维素钠10-20份，聚乙二醇5-15份，交联剂3-10份，增塑剂3-10份，水100-150份；其中水滑石的改性方法为：将水滑石加入浓度50%的乙醇水溶液中，加热至60℃，恒温搅拌2h，然后加入月桂醇醚磷酸酯钾盐，调节pH至4，在60℃下反应4h，过滤洗涤烘干即可。2.根据权利要求1所述的一种高阻隔性PVA基复合膜，其特征在于：所述水滑石的改性方法中水滑石与月桂醇醚磷酸酯钾盐的质量比为4-5:1。3.根据权利要求1所述的一种高阻隔性PVA基复合膜，其特征在于：所述增塑剂为三羟甲基丙烷或甘油中的任意一种。4.根据权利要求1所述的一种高阻隔性PVA基复合膜，其特征在于：所述交联剂为硼酸，聚乙二醇二缩水甘油醚和戊二醛的混合物。5.根据权利要求1所述的...