The invention discloses a heat-resistant bisphenol A plastic packaging bag, which is composed of the following weights of raw materials: phosphorous acid 3 4, high density polyethylene 120 150, tert-butyl-p-diphenol 0.7 1, bisphenol A1 2, heat-resistant stabilizer 1 2, tristearic glyceride 2 3, silicon powder 10 17, microcrystalline paraffin 4 6, lauryl dimethylamine oxide 0.8 1. Microcrystalline paraffin wax was treated with phenol A, and then esterified with phosphorous acid and ethanol as raw materials. Silicon powder was introduced into the esterification, which improved the surface activity of the microcrystalline silicon powder. After blending with toluene solution of microcrystalline paraffin wax treated with bisphenol A, the filler modified with bisphenol A was obtained, which could effectively improve the thermal stability and mechanical properties of the product.
【技术实现步骤摘要】
一种耐热双酚A型塑料包装袋及其制备方法
本专利技术属于包装袋领域，具体涉及一种耐热双酚A型塑料包装袋及其制备方法。
技术介绍
塑料包装袋是一种以塑料为原材料，用于生产生活中各种用品的包装袋，广泛用于日常生活和工业生产中，但是这一时的方便却带来长久的危害。常用的塑料包装袋多为聚乙烯薄膜制成，该薄膜无毒，故可用于盛装食品。还有一种薄膜为聚氯乙烯制成，聚氯乙烯本身也无毒性，但根据薄膜的用途所加入的添加剂往往是对人体有害的物质，具有一定的毒性。所以这类薄膜及由该薄膜做的塑料袋均不宜用来盛装食品；目前，大部分塑料袋的耐热稳定性差，在受到高温时，容易释放有毒物质，因此，如何提高塑料包装袋的耐热温度是目前研究的重点。
技术实现思路
本专利技术的目的在于针对现有技术的缺陷和不足，提供一种耐热双酚A型塑料包装袋及其制备方法。为实现上述目的，本专利技术采用以下技术方案：一种耐热双酚A型塑料包装袋，它是由下述重量份的原料组成的：亚磷酸3-4、高密度聚乙烯120-150、叔丁基对二苯酚0.7-1、双酚A1-2、耐热稳定剂1-2、三硬脂酸甘油酯2-3、硅微粉10-17、微晶石蜡4-6、月桂基二...
【技术保护点】
1.一种耐热双酚A型塑料包装袋，其特征在于，它是由下述重量份的原料组成的：亚磷酸3‑4、高密度聚乙烯120‑150、叔丁基对二苯酚0.7‑1、双酚A1‑2、耐热稳定剂1‑2、三硬脂酸甘油酯2‑3、硅微粉10‑17、微晶石蜡4‑6、月桂基二甲基氧化胺0.8‑1。
【技术特征摘要】
1.一种耐热双酚A型塑料包装袋，其特征在于，它是由下述重量份的原料组成的：亚磷酸3-4、高密度聚乙烯120-150、叔丁基对二苯酚0.7-1、双酚A1-2、耐热稳定剂1-2、三硬脂酸甘油酯2-3、硅微粉10-17、微晶石蜡4-6、月桂基二甲基氧化胺0.8-1。2.根据权利要求1所述的一种耐热双酚A型塑料包装袋，其特征在于，所述的耐热稳定剂为二月桂酸二丁基锡、硬脂酸锌中的一种。3.一种如权利要求1所述耐热双酚A型塑料包装袋的制备方法，其特征在于，包括以下步骤：(1)取微晶石蜡，加入到其重量4-7倍的甲苯中，搅拌均匀，加入双酚A，升...