The invention discloses a mixing ratio and method of building waste brick making, which is made from the following weight share raw materials: construction waste concrete with particle size less than 10 mm: 25 35 parts, construction waste brick powder with particle size less than 5 mm: 60 70 parts, cement: 10 15 parts. The invention utilizes fewer kinds of raw materials, reduces the production process and reduces the production cost, and the proportion of industrial waste in raw materials can reach more than 88%, which can effectively eliminate the pollution of construction waste to the environment, is an effective method of comprehensive utilization of resources, and has good application prospects.
【技术实现步骤摘要】
一种建筑垃圾制砖配比及方法
本专利技术属于建筑垃圾资源化利用
，具体涉及一种建筑垃圾制砖配比及方法。
技术介绍
伴随着建筑业的迅速发展，由建筑业产生的建筑垃圾也空前增加。国家也逐步加强对土地资源的保护，煤炭资源价格持续高昂，过去利用粘土烧结成砖的技术将逐步被淘汰，取而代之的将是无需烧结，主要原料为固废的非烧结砖。利用建筑垃圾来制备墙体砖，既消除了建筑垃圾堆放引发的环境问题，又提供了一种粘土实心烧结砖的替代产品。国内已经开展了部分利用建筑垃圾制备墙体砖的研究。综合来看，以往的建筑垃圾墙体砖工艺中，建筑垃圾处理效率低，原料个数多，胶凝材料成本较高，市场应用性较差。
技术实现思路
本专利技术的目的在于提供一种建筑垃圾制砖配比及方法，该砖能够符合中华人民共和国农业行业标准《混凝土普通砖和装饰砖》(NY/T671-2003)的要求，并且其生产方法具有建筑垃圾处理效率较高，生产成本较低的特点。本专利技术提供的建筑垃圾制砖配比及方法，由以下重量份额的原料制得：粒径在10mm以下的建筑垃圾废混凝土：25-35份，粒径在5mm以下的建筑垃圾废砖粉：60-70份，水泥：10-15份...
【技术保护点】
1.一种建筑垃圾制砖配比及方法，由以下重量份额的原料制得：粒径在10mm 以下的建筑垃圾废混凝土：25‑35份，粒径在5mm以下的建筑垃圾废砖粉： 60‑70份，水泥：10‑15份。
【技术特征摘要】
1.一种建筑垃圾制砖配比及方法，由以下重量份额的原料制得：粒径在10mm以下的建筑垃圾废混凝土：25-35份，粒径在5mm以下的建筑垃圾废砖粉：60-70份，水泥：10-15份。2.根据权利要求1所述的建筑垃圾混凝土砖，其特征在于：水泥为32.5普通硅酸盐水泥。3.权利要求1所述建筑垃圾制砖配比及方法，其步骤包括：(1...