A Multifunctional Single-guide Wet Fabric

The invention discloses a multi-functional single-guide wet fabric, which belongs to the field of textile technology and is woven by a double-sided knitting machine to form a double-sided grey fabric. The inner layer of the grey fabric forms a mesh structure by a ring-collecting weaving method. The outer surface area of the grey fabric is larger than the inner layer, and the yarn forming the inner layer is polyethylene yarn or polyethylene composite fiber yarn. The outer yarn is a yarn with good water absorption. The multi-functional single-guide wet fabric of the invention is a double-sided knitted mesh fabric, which is cool, smooth, easy to dye and has the function of single-guide wet and anti-ultraviolet ray.

【技术实现步骤摘要】
一种多功能单向导湿面料
本专利技术涉及纺织
，特别涉及一种多功能单向导湿面料。
技术介绍
当代人对穿着和家居用品除了美观提出越来越多功能性、舒适性的要求。在炎热的夏季，人体对纺织面料的诉求主要是凉爽和干燥。为了提高面料的凉爽度，市场往往采用高导热能力的纱线织平整高克重的面料提交接触冷感，缺点是面料厚重，透气性差。人体大量出汗后，如果接触身体的面料不吸汗，人体会感觉闷热，而吸湿能力好的面料，吸汗后干燥往往需要一段时间，在这段时间内面料容易贴附在人体身上，使人感觉潮湿粘腻。为了解决这个问题，单向导湿的面料开始受到青睐，目前市场上单向导湿面料的主要实现方法是，通过物理或者化学的方法是面料接触人体的内侧拒水，不接触人体的织物外侧吸水，人体出汗时，会通过织物缝隙接触到外层织物并被快速吸收扩散，从而保持内层的干爽。如专利文献CN104757724A中公开了一种吸湿速干壳聚糖棉针织面料，该面料外层采用壳聚糖/棉纤维，内层采用丙纶纤维；专利文献CN102899795B公开了多功能双层针织面料，内层为丙纶纤维，外层为涤纶纤维，这种方法的缺点是内层使用的拒水纤维一般是吸湿能力差的丙纶或者涤纶，虽然本文档来自技高网...

【技术保护点】
1.一种多功能单向导湿面料，其特征在于是通过双面针织机进行织造形成双面结构的坯布，所述坯布的里层是通过集圈的织法形成网孔结构，所述坯布外层的表面积大于所述里层，形成所述里层的纱线为聚乙烯纱线或聚乙烯复合纤维纱线，形成所述外层的纱线为吸水性好的纱线。

【技术特征摘要】
1.一种多功能单向导湿面料，其特征在于是通过双面针织机进行织造形成双面结构的坯布，所述坯布的里层是通过集圈的织法形成网孔结构，所述坯布外层的表面积大于所述里层，形成所述里层的纱线为聚乙烯纱线或聚乙烯复合纤维纱线，形成所述外层的纱线为吸水性好的纱线。2.根据权利要求1所述的一种多功能单向导湿面料，其特征在于：所述坯布外层为平纹结构。3.根据权利要求1所述的一种多功能单向导湿面料，其特征在于：所述聚乙烯复合纤维为聚乙烯/聚酰胺、聚乙烯/聚酯或聚乙烯/聚丙烯。4.根据权利要求3所述的一种多功能单向导湿面料，其特征在于：所述聚乙烯复合纤维的纤度为50D～400D，单丝的纤度小于4...