The invention relates to a manufacturing method of enameled wire with square cross section shape, belonging to the technical field of enameled wire. The method of the invention includes: 1) drawing copper wires to obtain the required thickness of strip wires; (02) calendering the wires after drawing, and calendering the strip wires into flat wires; (203) shaping the wires with flat shapes by means of dies, and shaping them into regular wires with square cross-section shapes; and (04) calendering the wires with square cross-section shapes. The insulating film is coated on the outside of the conductor, and the enameled wire is formed by winding the wire. The enameled wire manufactured by the invention has high dimensional accuracy, uniform film thickness and high electric energy conversion rate.
【技术实现步骤摘要】
一种具有方形截面形状的漆包线制造方法
本专利技术涉及漆包线
，尤其涉及一种具有方形截面形状的漆包线制造方法。
技术介绍
漆包线由导体和绝缘层两部分组成，其广泛用作电动机、编译器等电机的线圈用电线。漆包线一般是将裸线经退火软化，然后再经过多次涂漆，烘焙而成。漆包线分为圆漆包线和扁平漆包线，扁平漆包线与圆漆包线相比，电能转化效率更高，且具有更佳的柔软性和挠性，特别适合用于电气、电子设备。专利技术专利CN106409403B公开了一种扁平漆包线制造工艺，并具体公开了该工艺包括：（1）熔炼铜铝合金，轧制、拉伸，直至得到所需厚度的条形合金导线；（2）配置抗氧化层用覆层液，条形合金导线浸入注满覆层液的容器中，使条形合金导线表面包裹所需厚度的抗氧化层；（3）在抗氧化层的两侧，依次涂覆所需厚度的聚氨酯、自粘漆和润滑剂，即得。该专利技术从原材料的角度进行改进，减少了铜材料的使用量，使得制成的漆包线三相电阻比一般铜漆包线低，且该漆包线空载转速、最大扭矩等各项性能更优。
技术实现思路
本专利技术针对现有技术存在的问题，提出了一种漆包线尺寸精度高、漆膜均匀的具有方形截面形状的漆包线制造...
【技术保护点】
1.一种具有方形截面形状的漆包线制造方法，其特征在于，包括：步骤S01，将铜线拉丝得到所需厚度的条形导线；步骤S02，对拉丝后的导线进行压延处理，将条形导线压延呈扁平状的导线；步骤S03，利用模具将扁平状的导线进行整形处理，整形为规整的具有方形截面形状的导线；步骤S04，在具有方形截面形状的导线外涂覆绝缘膜；步骤S05，绕线获得成型漆包线。
【技术特征摘要】
1.一种具有方形截面形状的漆包线制造方法，其特征在于，包括：步骤S01，将铜线拉丝得到所需厚度的条形导线；步骤S02，对拉丝后的导线进行压延处理，将条形导线压延呈扁平状的导线；步骤S03，利用模具将扁平状的导线进行整形处理，整形为规整的具有方形截面形状的导线；步骤S04，在具有方形截面形状的导线外涂覆绝缘膜；步骤S05，绕线获得成型漆包线。2.根据权利要求1所述的一种具有方形截面形状的漆包线制造方法，其特征在于，所述步骤S01进一步包括：步骤S11，利用中拉机将硬质铜线从原材料状态拉丝成中型尺寸的条形导线；步骤S12，利用微拉机将中型尺寸的条形导线拉丝成微型尺寸的条形导线。3.根据权利要求1所述的一种具有方形截面形状的漆包线制造方法，其特征在于，步骤S03具体为：利用模具将扁平状的导线进行整形，整形为截面四角处具...
【专利技术属性】
技术研发人员：沈晓宇，
申请(专利权)人：浙江东尼电子股份有限公司，
类型：发明
国别省市：浙江,33
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。