The invention discloses a flotation separation process for copper-lead sulfide ore, which grinds copper-lead sulfide ore to a mass percentage of 70%-95% with a particle fineness less than 0.074 mm; adjusts the mass percentage concentration of pulp by adding water to the grinding product to 25%-35%; adds a mixture of 200 g/t-1500 g/t of iron sulfate and magnesium chloride to the pulp as a combined depressant, and adds a mixture of 40 g/t-120 g/t of ethylthiamine. A combined collector consisting of ester, O isooctyl N ethoxycarbonyl thiamine ester and 4 terpene alcohol is used for flotation; the flotation separation of copper lead sulfide ore is realized by the present invention, which has simple process, low reagent cost, high concentrate quality and no environmental pollution.
【技术实现步骤摘要】
一种硫化铜铅矿的浮选分离工艺
本专利技术涉及一种硫化铜铅矿的浮选分离工艺，属于矿物加工
技术介绍
铜、铅作为关系国计民生的主要金属矿产品，可用于工农业生产的诸多领域。随着经济的发展，铜、铅矿产资源得到大规模开采利用，使得资源量日益紧缺，难选矿石的处理量日益增加，矿石的处理难度日益加大，尤其是含有铜、铅矿物的矿石的浮选分离更加困难；同时随着人们开始对环境保护和降低能源消耗越来越重视，对资源利用、能源消耗以及生产工艺提出了越来越高的要求。目前，国内外对于硫化铜、铅矿石的回收主要采用的是浮选法。对于硫化铜、铅矿物的浮选分离目前研究最多的流程结构有：（1）铜、铅矿物优先浮选流程；（2）铜、铅矿物混合浮选抛尾-混合精矿优先浮选分离流程；（3）等可浮选流程，等等。铜铅浮选分离的方案一般有两种，一是浮铜抑铅，二是浮铅抑铜。常用的浮铜抑铅方法有重铬酸盐法、氰化物法和加温法等，但是重铬酸盐法和氰化物法对生态环境污染非常严重，加温法操作复杂，难以控制，应用难度大；常用的浮铅抑铜法一般采用氰化物或以氰化物为主的混合物作为抑制硫化铜矿物的抑制剂，由于环保压力和氰化物对贵金属的溶...
【技术保护点】
1.一种硫化铜铅矿的浮选分离工艺，其特征在于，具体步骤如下：（1）将硫化铜铅矿磨矿，磨矿至颗粒细度小于0.074mm的质量百分比为70%～95%；（2）将步骤（1）的磨矿产品加水调节矿浆的质量百分比浓度为25%～35%；（3）在步骤（2）的矿浆中添加200g/t～1500g/t的硫酸铁和氯化镁的混合物为硫化铅矿的组合抑制剂，添加40g/t～120g/t由乙硫氨酯、O‑异辛基‑N‑乙氧羰基硫氨酯、4‑萜烯醇组成的组合捕收剂进行浮选。
【技术特征摘要】
1.一种硫化铜铅矿的浮选分离工艺，其特征在于，具体步骤如下：（1）将硫化铜铅矿磨矿，磨矿至颗粒细度小于0.074mm的质量百分比为70%～95%；（2）将步骤（1）的磨矿产品加水调节矿浆的质量百分比浓度为25%～35%；（3）在步骤（2）的矿浆中添加200g/t～1500g/t的硫酸铁和氯化镁的混合物为硫化铅矿的组合抑制剂，添加40g/t～120g/t由...
【专利技术属性】
技术研发人员：赵刘闯，刘全军，梁远琴，江旭，纪慧超，余力，罗斌，
申请(专利权)人：昆明理工大学，
类型：发明
国别省市：云南,53
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。