A method for improving the bonding strength of diamond wire coating is presented. When the busbar passes through the outlet end, the nickel layer is plated on the diamond wire through alkali washing, hot water washing, cold water washing, acid washing and pre-plating reinforcement. During the whole process, alkali washing plays the role of removing grease on the surface of diamond wire, acid washing plays the role of removing oxide on the surface of diamond wire, so that when the diamond wire passes through pre-plating and strengthening processes, a strong coating bonding force can be obtained. After pre-plating and strengthening the nickel layer on the steel wire, a more solid coating can be obtained, and the rate of peeling and brittle fracture can be greatly reduced, thus the stability can be obtained. The fixed coating improves the binding force of the coating and the quality of the product.
【技术实现步骤摘要】
一种提高金刚线镀层结合力的方法
本专利技术涉及电镀金刚石线锯生产线，具体涉及一种提高金刚线镀层结合力的方法。
技术介绍
如今崭新的技术金钢线切片技术，将在光伏硅片使用比例逐步提高，无论是单晶还是多晶。金钢线切片的技术最主要的优势体现在这两个方面：硅耗的降低和切割效率的提升。金钢线和砂浆切割的基本区别，金钢线是将金刚石采用粘接和电镀的方式固定在直拉钢线上进行高速往返切削，而砂浆的切割方式是游离式的切割模式，靠悬浮液的悬浮碳化硅，再通过线网的带动，进行磨削切割。金钢线为什么能够将效率提升？主要有以下几个原因：1、固结方式，也就是带来金刚石参与磨削的切割更多，同时也减少了磨料之间的相互磨损现象。2、金刚石硬度高，金刚石的耐磨损强，都将大大延长金钢线的使用寿命。3、切割线速度高，金刚石与硅片接触面积增大，金钢石线又将能承受高线速度带来的其他不良，从而发挥高切割速度的优势。传统砂浆的利用钢丝的快速运动将含磨料的液体带入到工件切缝中，产生切削作用。在切割过程中，碳化硅被冲刷下来，唯有持续进行滚动磨削，而减少切割效率。碳化硅的硬度9.5(莫氏)，而金刚石硬度在10(莫氏)。金钢...
【技术保护点】
1.一种提高金刚线镀层结合力的方法，其特征在于：当母线经放线端再依次经过碱洗‑热水洗‑冷水洗‑酸洗‑冷水洗‑预镀加固工序给金刚线镀上镍层。
【技术特征摘要】
1.一种提高金刚线镀层结合力的方法，其特征在于：当母线经放线端再依次经过碱洗-热水洗-冷水洗-酸洗-冷水洗-预镀加固工序给金刚线镀上镍层。2.根据权利要求1所述的一种提高金刚线镀层结合力的方法，其特征在于：所述的碱洗槽配比浓度5-10％，清洗时间15秒，温度设定60-65℃。3.根据权利要求2所述的一种提高金刚线镀层结合力的方法，其特征在于：所述的碱洗分为两道，第一道碱洗，将母线置于第一碱洗池中进行第一道碱洗，碱洗槽配比浓度5-10％，清洗时间15秒，温度设定60-65℃；第二道碱洗，将母线置于含有清洗剂的碱性清洗池中进行第二道碱洗，去除母线表面油脂及其他污物，所述第二道碱洗中增加超声振板。4.根据权利要求1所述的一种提高金刚线镀层结合力的方法，其特征在于：所述的热水洗步骤使用纯水，清洗时间15秒，温度设定60-65℃...
【专利技术属性】
技术研发人员：李宏光，汪明仰，
申请(专利权)人：安徽卡尔森新材料科技有限公司，
类型：发明
国别省市：安徽,34