用于锂电池负极的片状硅粒制造技术

本发明专利技术公开了用于锂电池负极的片状硅粒，属于硅材料制备技术领域；包括片状单质硅内芯，所述的片状单质硅内芯上下表面具有氧化硅外层，所述的氧化硅外层上贯通分布有多个孔洞；本发明专利技术的硅颗粒结构，有利于与石墨充分混合形成分支状及网络状结构，有利于缓解硅的体积效应，满足锂电池硅碳负极中对硅材料的要求，实现金刚线切割废料的再利用，并实现巨大的经济效益。

Flake Silicon Particles for Negative Electrodes of Lithium Batteries

The invention discloses sheet silicon particles for lithium battery negative electrode, belonging to the technical field of silicon material preparation; including sheet silicon inner core, the upper and lower surfaces of the sheet silicon inner core have silicon oxide outer layer, and the silicon outer layer is perforated with multiple holes; the silicon particle structure of the invention is advantageous to fully mix with graphite to form branching and network structure, and is advantageous to the formation of a branching and network structure. In order to alleviate the volume effect of silicon, meet the requirements of silicon materials for lithium battery silicon carbon anode, realize the reuse of WEDM waste, and achieve great economic benefits.

【技术实现步骤摘要】
用于锂电池负极的片状硅粒
本专利技术属于硅材料制备
，具体涉及用于锂电池负极的片状硅粒。
技术介绍
锂离子电池是目前储能技术中应用最广泛的储能电芯，提高电芯能量存储密度是全世界追求的目标，电芯能量密度的提高主要依赖于其正、负极材料的发展进步。人们普遍采用碳基负极材料作为锂离子电池的负极材料，但碳基负极材料能量密度低(理论比容量372mAh/g，实际可逆比容量为330mAh/g)。硅是目前已知比容量（理论比容量4200mAh/g）最高的锂离子电池负极材料，但由于其巨大的体积效应（>300%），硅电极材料在充放电过程中会粉化而从集流体上剥落，使得活性物质与活性物质、活性物质与集流体之间失去电接触，同时不断形成新的固相电解质层SEI，最终导致电化学性能的恶化。晶体硅切片约40%的材料通过金刚线切割变成粉末流失，以多晶硅棒为例，2018年8月份每公斤约105元，2018年上半年产量约50GW，折合晶棒约20万吨，切片流失40%，折合10万吨，而且该粉末粒径过小（粒径分布200nm~2.5um），常规方法无法处理，对环境保护形成较大的压力。
技术实现思路
本专利技术克服现有技术本文档来自技高网...

【技术保护点】
1.用于锂电池负极的片状硅粒，其特征在于，包括片状单质硅内芯（1），所述的片状单质硅内芯（1）上下表面具有氧化硅外层（2），所述的氧化硅外层（2）上贯通分布有多个孔洞（3）。

【技术特征摘要】
1.用于锂电池负极的片状硅粒，其特征在于，包括片状单质硅内芯（1），所述的片状单质硅内芯（1）上下表面具有氧化硅外层（2），所述的氧化硅外层（2）上贯通分布有多个孔洞（3）。2.根据权利要求1所述的用于锂电池负极的片状硅粒，其特征在于，所述的片状硅粒的厚度为...