复合节能门窗的可抗菌涂料制造技术

本发明专利技术公开了一种复合节能门窗的可抗菌涂料，按照质量百分比，包括：钛白粉20％‑30％、灰石粉15％‑20％、佩利多1％‑3％、皂土2％‑4％、苯乙烯‑丙烯酸酯乳液5％‑10％、硅溶胶15％‑20％、羟乙基纤维素0.1％‑0.5％、填料10％‑15％、胶原纤维1％‑3％、无机颜料5％‑10％、碧玺粉0.5％‑1％、汉麻纤维粉0.2％‑0.6％、水5％‑20％、分散剂2％‑4％、消泡剂0.2％‑0.5％、增稠剂1％‑2％。本发明专利技术的优点在于，具有较好的成膜特性以及使用效果。

Antibacterial coatings for composite energy-saving doors and windows

The invention discloses an antibacterial coating for composite energy-saving doors and windows, according to the mass percentage, including: titanium white powder 20%, 30%, limestone powder 15%, 20%, pilto 1% 1% 3%, bentonite 2% 4%, styrene acrylic emulsion 5% 5% 10%, silica sol 15% 15%, hydroxyethyl cellulose 10%, filler filler, collagen fiber, and inorganic. Pigment 5%10%, Bixie powder 0.5%1%, hemp fiber powder 0.2%0.6%, water 5%20%, dispersant 2%4%, defoamer 0.2%0.5%, thickener 1%2%. The advantages of the present invention are that it has better film forming characteristics and application effect.

【技术实现步骤摘要】
复合节能门窗的可抗菌涂料
本专利技术涉及一种涂料，尤其是复合节能门窗的可抗菌涂料。
技术介绍
节能门窗是为了增大采光通风面积或表现现代建筑的性格特征的一种门窗。节能门窗会提高材料的光学性能、热工性能和密封性，改善门窗的构造来达到预计效果。节能门窗应该从以下几个方面进行考量：一、门窗材质；二、玻璃；三、门窗节能是整体的节能。总而言之，门窗的节能不仅取决于材质，还取决于玻璃，更取决于门窗的工艺。从门窗材料来看，目前有铝合金断热型材、铝木复合型材、钢塑整体挤出型材以及UPVC塑料型材等一些技术含量较高的节能产品，其中使用较广的是UPVC塑料型材，它所使用的原料是高分子材料--硬质聚氯乙烯。为了解决大面积玻璃造成能量损失过大的问题，将普通玻璃加工成中空玻璃、镀膜玻璃、高强度LOW-E防火玻璃、采用磁控真空溅射放射方法镀制含金属层的玻璃以及最特别的智能玻璃。(1)建筑门窗和建筑幕墙全周边高性能密封技术。降低空气渗透热损失，提高气密、水密、隔声、保温、隔热等主要物理性能。(2)高性能中空玻璃和经济型双玻系列产品工艺技术和产品性能上要有较大突破。重点解决热反射和低辐射中空玻璃、高性能安全中空玻璃以本文档来自技高网...

【技术保护点】
1.一种复合节能门窗的可抗菌涂料，其特征在于，按照质量百分比，包括：钛白粉20％‑30％、灰石粉15％‑20％、佩利多1％‑3％、皂土2％‑4％、苯乙烯‑丙烯酸酯乳液5％‑10％、硅溶胶15％‑20％、羟乙基纤维素0.1％‑0.5％、填料10％‑15％、胶原纤维1％‑3％、无机颜料5％‑10％、碧玺粉0.5％‑1％、汉麻纤维粉0.2％‑0.6％、水5％‑20％、分散剂2％‑4％、消泡剂0.2％‑0.5％、增稠剂1％‑2％。

【技术特征摘要】
1.一种复合节能门窗的可抗菌涂料，其特征在于，按照质量百分比，包括：钛白粉20％-30％、灰石粉15％-20％、佩利多1％-3％、皂土2％-4％、苯乙烯-丙烯酸酯乳液5％-10％、硅溶胶15％-20％、羟乙基纤维素0.1％-0.5％、填料10％-15％、胶原纤维1％-3％、无机颜料5％-10％、碧玺粉0.5％-1％、汉麻纤维粉0.2％-0.6％...

【专利技术属性】
技术研发人员：赵辉，赵俊，吴安学，赵源泉，韩荣富，李随有，钱德富，
申请(专利权)人：巢湖市兰天大诚门窗幕墙有限公司，
类型：发明
国别省市：安徽,34