本发明专利技术公开了一种抑菌氨基模塑料，原料组分按照重量分计包括：甲醛60‑75份、尿素70‑80份、尿醛树脂80‑100份、聚碳酸酯树脂60‑70份、柏木油15‑25份、偶联剂3‑5份、固化剂5‑8份、抑菌剂3‑5份。本发明专利技术的抗菌塑料，具有强效抑制细菌、杀灭细菌和防霉的效果，可用于生产减磨耐磨零件、传动零件，以及化工，仪表等。

An Antibacterial Amino Molding Plastic

The invention discloses a bacteriostatic amino moulding plastic, whose raw material components are divided into 60 to 75 parts of formaldehyde, 70 to 80 parts of urea, 80 to 100 parts of urea-formaldehyde resin, 60 to 70 parts of polycarbonate resin, 15 to 25 parts of cedar oil, 3 to 5 parts of coupling agent, 5 to 8 parts of curing agent and 3 to 5 parts of bacteriostatic agent. The Antimicrobial Plastics of the invention has the effects of strong inhibition of bacteria, killing bacteria and mildew, and can be used to produce wear-resistant and wear-resistant parts, transmission parts, chemical industry, instrumentation, etc.

【技术实现步骤摘要】
一种抑菌氨基模塑料
本专利技术属于塑料材料
，具体涉及一种抑菌氨基模塑料。
技术介绍
氨基模塑料的主要成分包括氨基塑料和脲醛树脂胶。其中，氨基塑料，也称电玉粉，其组成成分常见的可以为尿醛树脂(UF)+密胺树脂(MF)+石棉，具有自熄性、防毒性、耐电弧性、耐热性、易着色等性质，广泛应用于日用品，餐具，电器零件，泡沫塑料、隔音材料等。脲醛树脂胶是以甲醛和尿素为原料，在一定条件下进行加成反应和缩聚反应而制成的胶粘剂。氨基模塑料用量日益增大，产品越来越多，最常受到的技术难题则是如何提高其抑菌性的能力，以应对不断扩大的市场需求，成为本行业发展的重要研究方向。
技术实现思路
专利技术目的：为了克服现有技术中存在的不足，本专利技术提供一种抑菌氨基模塑料，提高了氨基模塑料颗粒成品的抑菌性，且质量稳定。技术方案：为实现上述目的，本专利技术采用如下技术方案：一种抑菌氨基模塑料，原料组分按照重量分计包括：甲醛60-75份、尿素70-80份、尿醛树脂80-100份、聚碳酸酯树脂60-70份、柏木油15-25份、偶联剂3-5份、固化剂5-8份、抑菌剂3-5份。进一步的，所述偶联剂为锆类偶联剂、钛酸酯类偶联剂本文档来自技高网...

【技术保护点】
1.一种抑菌氨基模塑料，其特征在于：原料组分按照重量分计包括：甲醛60‑75份、尿素70‑80份、尿醛树脂80‑100份、聚碳酸酯树脂60‑70份、柏木油15‑25份、偶联剂3‑5份、固化剂5‑8份、抑菌剂3‑5份。

【技术特征摘要】
1.一种抑菌氨基模塑料，其特征在于：原料组分按照重量分计包括：甲醛60-75份、尿素70-80份、尿醛树脂80-100份、聚碳酸酯树脂60-70份、柏木油15-25份、偶联剂3-5份、固化剂5-8份、抑菌剂3-5份。2.根据权利要求1所述的一种抑菌氨基模塑料，其特征在于：所述偶联剂为锆类偶联剂、钛酸酯类偶联剂中的一种或其混合物。3.根据权利要求1所述的一种抑菌氨基模塑料，其特征在于：所述固化剂为邻苯二甲酸...