The invention belongs to the technical field of macromolecule materials, and provides a mineral reinforced high-gloss ABS and its preparation method. The main material is prepared by weight components of ABS 60-80 phr, talc powder 20-30 phr and magnesium sulfate whisker 0-10 phr. Based on 100 phr of total weight of the main material, the auxiliary material is composed of 0.1-0.3 phr of antioxidant, 0.1-1 phr of special toughener and 0.1-1 phr of special toughener. Composition of lubricant is 0.5-2 phr. The reinforced ABS material prepared by the invention has good processing performance and thermal stability, simple preparation process, environmental protection, high gloss of injection products, mirror effect and little damage to the mould.
【技术实现步骤摘要】
一种矿物增强高光ABS及其制备方法
本专利技术属于高分子材料
，具体涉及一种矿物增强高光ABS及其制备方法。
技术介绍
玻璃纤维增强ABS由于良好的韧性、高模量高耐热和较低的线性膨胀系数，同时借助RHCM模具可以实现高光效果，因此长期以来在电视机前框领域中有着广泛应用。但是由于材料中玻纤的存在，制品中经常出现浮纤等外观不良，而且长时间注塑，对模具的损伤较为严重。玻璃纤维为强度极高的针状结构，在注塑过程中容易出现模具表面损伤。同时由于玻纤和树脂的流动性差异，模温较低导致质量轻、冷凝快的玻璃纤维优先在模具表面凝结，不能被塑胶融体充分包围而产生浮纤，影响制件外观。常规使用的玻纤增强ABS材料，按照每个班次12h计算，平均每个班次需要对模具简单抛光2～3次，每次30min左右，对于损伤严重的模具，甚至需要拆卸模具进行维修，耗费大量人力和物力。矿粉相比玻璃纤维没有较高的长径比，其外观为普通粒状，本身硬度比玻纤纤维要软，因此注塑过程与模具的摩擦力更小，在很大程度上可以减少模具维护时间。对于上述问题，我司已在PC+GF领域申请相关专利CN106751677A，但在ABS+...
【技术保护点】
1.一种矿物增强高光ABS，其特征在于：由主料和辅料按重量份制备而成，其中主料是由以下组分按重量份制备而成：ABS 60～80份，滑石粉20～30份，硫酸镁晶须0～10份；以主料总重量份为100份为基准，所述辅料是由以下组分按重量份制备而成：抗氧剂0.1～0.3份，特殊增韧剂0.1～1份，润滑剂0.5～2份。
【技术特征摘要】
1.一种矿物增强高光ABS，其特征在于：由主料和辅料按重量份制备而成，其中主料是由以下组分按重量份制备而成：ABS60～80份，滑石粉20～30份，硫酸镁晶须0～10份；以主料总重量份为100份为基准，所述辅料是由以下组分按重量份制备而成：抗氧剂0.1～0.3份，特殊增韧剂0.1～1份，润滑剂0.5～2份。2.根据权利要求1所述的矿物增强高光ABS，其特征在于：所述抗氧剂由主抗氧剂β-(3,5-二叔丁基-4-羟基苯基)丙酸正十八碳醇酯和辅抗氧剂三-(2，4-二叔丁基苯基)亚磷酸酯按质量比1：1组成。3.根据权利要求1所述的矿物增强高光...
【专利技术属性】
技术研发人员：丁有朝，魏子芳，任东方，李荣群，
申请(专利权)人：重庆会通科技有限公司，
类型：发明
国别省市：重庆,50
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。