The invention discloses a highly flame-retardant cable material formula, which consists of the following raw materials: resin 30 35, phthalate 20 28, liquid wax 6 12, hard barium 22 33, paraffinic acid 9 11, internal and external slippers 15 25, antioxidant 19 28, PVC 60 76, dibasic phosphite 12 16, dioctyl phthalate 9.6 9.9, stearic acid. Lead, 12.29, chlorinated paraffin 20.36, calcium stearate 6.9, petroleum ester 20.30, chlorinated paraffin 28.29, calcium stearate 6.8, calcium carbonate 25.29. The product of the invention has good heat resistance and aging resistance, can adapt to the high temperature caused by overload and short circuit during the use of power cables, has high insulation strength and volume resistivity, small friction coefficient on the inner surface, is convenient for use, and has long service life.
【技术实现步骤摘要】
一种高度阻燃的电缆材料
本专利技术涉及一种高度阻燃PVC电缆材料。
技术介绍
PVC护套具有柔软、随意弯曲折叠、相对厚度薄、体积小、连接简单、拆卸方便等优点，可以任意选择导线数目及间距，使联线更方便，大大减少产品的体积，减少生产成本，提高生产效率，适合电器设备中作数据传输线缆或动力传输之用。而传统的PVC电缆护套由于自身配料不合理，致使制造成的护套抗拉强度较低，韧性差，无法继续对包裹在护套内部的电缆导体起到保护作用，使用寿命较短；在电缆的使用过程中，出于安全考虑，也需要进一步提高电缆护套的阻燃性能。鉴于以上现有技术中存在的缺陷，有必要将其进一步改进，使其更具备实用性，才能符合实际使用情况。
技术实现思路
为了克服上述现有技术的缺陷，本专利技术的目的是提供一种高度阻燃PVC电缆材料。专利技术是采取以下技术方案来实现的：一种高度阻燃PVC电缆材料，其特征在于，它由以下原料组成：按份量计取，树脂30-35份、液体蜡6-12份、硬钡22-33份、内外滑剂15-25份、抗氧化剂19-28份、PVC60-76份、二碱式亚磷酸12-16份、邻苯二甲酸二辛酯9.6-9.9份、硬脂酸铅、12-29份、氯化石蜡20-36份、硬脂酸钙6-9份、石油酯20-30份、氯化石蜡28-29份、硬脂酸钙6-8份、碳酸钙25-29份。具体地，本专利技术由以下原料：所述按重量份计取，树脂30份、液体蜡10份、脂蜡酸10份、内外滑剂20份、抗氧化剂22份、PVC70份、二碱式亚磷酸15份、邻苯二甲酸二辛酯9.8份、硬脂酸铅、26份、氯化石蜡30份、硬脂酸钙8份、石油酯28份、氯化石蜡28份、硬脂酸...
【技术保护点】
1.一种高度阻燃的电缆材料，其特征在于，它由以下原料组成：按份量计取，树脂30‑35份、邻苯20‑28份、液体蜡6‑12份、硬钡22‑33份、脂蜡酸9‑11份、内外滑剂15‑25份、抗氧化剂19‑28份、PVC60‑76份、二碱式亚磷酸12‑16份、邻苯二甲酸二辛酯9.6‑9.9份、硬脂酸铅、12‑29份、氯化石蜡20‑36份、硬脂酸钙6‑9份、石油酯20‑30份、氯化石蜡28‑29份、硬脂酸钙6‑8份、碳酸钙25‑29份。
【技术特征摘要】
1.一种高度阻燃的电缆材料，其特征在于，它由以下原料组成：按份量计取，树脂30-35份、邻苯20-28份、液体蜡6-12份、硬钡22-33份、脂蜡酸9-11份、内外滑剂15-25份、抗氧化剂19-28份、PVC60-76份、二碱式亚磷酸12-16份、邻苯二甲酸二辛酯9.6-9.9份、硬脂酸铅、12-29份、氯化石蜡20-36份、硬脂酸钙6-9份、石油酯20-30份、氯化石蜡2...