The invention relates to a starch based foam material and a preparation method thereof. In terms of extrusion foaming process for preparing starch based foam materials, the molding foaming process is simple, the surface layer has high density and many internal pores, and the starch based foam material with complex shape can be prepared. Besides, the process for preparing foam materials by rubber is realized by means of a mixer and an open mixer. Based on the plasticization of starch, the blending of components and the molding of materials, a new preparation method of starch based foams has been developed, and the application of starch based foams has been widened.
【技术实现步骤摘要】
一种淀粉基泡沫材料及其制备方法
本专利技术属于材料制备
，涉及一种物流包装盒内的缓冲物，具体涉及一种淀粉基泡沫材料及其制备方法。
技术介绍
现有应用于包装盒中的缓冲物主要以石油为原料，通过挤出、吹塑工艺制成。工艺过程简单，原料聚苯乙烯（EPS），主要来源于石油资源，其价格低廉，生产工艺成熟，已工业化使用。而目前的产品缺陷很多，比如EPS具有抗老化，防腐蚀等特点，所以在自然界不易腐烂，也不易降解，若深埋，会污染地下水源，破坏土壤结构；若焚烧处理，严重污染空气及大气环境；若回收利用，工作量大，成本高；其次，EPS来源于石油，属于不可再生资源，不可循环使用。
技术实现思路
为了克服上述现有技术的不足，本专利技术的目的是提供一种淀粉基泡沫材料及其制备方法，解决现有技术中石油资源的不可再生性，EPS泡沫材料的不可降解性、严重危害水源、大气等，造成了严重的环境问题。为了实现上述目的，本专利技术采用的技术方案是：一种淀粉基泡沫材料，按质量百分比包括以下组成：糊化淀粉：10-30%，聚乙烯醇PVA：20-50%，润胀淀粉：90-70%，塑化剂：35-50%，蒙脱土：1-5%，硬...
【技术保护点】
1.一种淀粉基泡沫材料，其特征在于，按质量百分比包括以下组成：糊化淀粉：10‑30%，聚乙烯醇PVA：20‑50%，润胀淀粉：90‑70%，塑化剂：35‑50%，蒙脱土：1‑5%，硬脂酸镁：1‑3%，瓜尔胶：1‑3%，偶氮二甲基酰胺：1‑5%。
【技术特征摘要】
1.一种淀粉基泡沫材料，其特征在于，按质量百分比包括以下组成：糊化淀粉：10-30%，聚乙烯醇PVA：20-50%，润胀淀粉：90-70%，塑化剂：35-50%，蒙脱土：1-5%，硬脂酸镁：1-3%，瓜尔胶：1-3%，偶氮二甲基酰胺：1-5%。2.根据权利要求1所述的一种淀粉基泡沫材料，其特征在于，所述的塑化剂为乙二醇、丙三醇、甲酰胺等小分子多元醇或氨基化合物。3.据权利要求1所述的一种淀粉基泡沫材料，其特征在于，所述的淀粉总量为80-100g，糊化淀粉占淀粉总量10-30%，润胀淀粉占淀粉总量90-70%。4.一种淀粉基泡沫材料的制备方法，其特征在于，包括以下步骤：1）将20-50%聚乙烯醇PVA，按照聚乙烯醇水溶液的质量分数为10-30%进行配比，并搅拌均匀，放置于65℃-80℃下溶解得到透明胶黏液体，冷却24h备用，得到处理后聚乙烯醇PVA；2...
【专利技术属性】
技术研发人员：林涛，张希娟，殷学风，袁枚，田杏欢，范晶，段敏，李静，
申请(专利权)人：陕西科技大学，
类型：发明
国别省市：陕西,61
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。