The invention discloses an impact resistant and high temperature resistant plexiglass, whose raw materials include: methyl methacrylate 70 75, butyl acrylate 7 9, octyl acrylate 7 9, dibutyl tin dimethacrylate 5 10 20, nanokaolin 10 20, initiator 1 2, crosslinking agent 3 5 by weight. The invention increases the impact resistance of the invention by introducing long carbon chain, adding suitable crosslinking agent to form a copolymer with network structure, adding nano-kaolin to increase the crosslinking point of the copolymer to prevent crack propagation in many aspects, and introduces suitable tin content in the copolymer, so as to improve the impact resistance of the invention while making the invention have better resistance. High temperature performance.
【技术实现步骤摘要】
一种抗冲击耐高温有机玻璃
本专利技术涉及有机玻璃
，尤其涉及一种抗冲击耐高温有机玻璃。
技术介绍
聚甲基丙烯酸甲酯(PMMA)是一种重要的有机透明材料又称为有机玻璃，它具有优异的光学性能，化学稳定性，耐候性和电绝缘性，广泛应用于各个领域，但有机玻璃的质地较脆，抗冲击强度较低，耐高温性能较低，从而限制了有机玻璃的应用。
技术实现思路
基于
技术介绍
存在的技术问题，本专利技术提出了一种抗冲击耐高温有机玻璃，本专利技术具有良好的抗冲击性能和耐高温性能。本专利技术提出的一种抗冲击耐高温有机玻璃，其原料按重量份包括：甲基丙烯酸甲酯70-75份，丙烯酸丁酯7-9份，丙烯酸辛酯7-9份，双甲基丙烯酸二丁基锡5-10份，纳米高岭土10-20份，引发剂1-2份，交联剂3-5份。优选地，甲基丙烯酸甲酯、丙烯酸丁酯、丙烯酸辛酯、双甲基丙烯酸二丁基锡的重量比为75：7：7：10。优选地，甲基丙烯酸甲酯与纳米高岭土的重量比为75：15。优选地，引发剂为过氧化二异丙苯。优选地，交联剂为丙烯酸烯丙酯。优选地，在抗冲击耐高温有机玻璃的制备过程中，将丙烯酸丁酯、丙烯酸辛酯、双甲基丙烯酸二丁基锡、纳...
【技术保护点】
1.一种抗冲击耐高温有机玻璃，其特征在于，其原料按重量份包括：甲基丙烯酸甲酯70‑75份，丙烯酸丁酯7‑9份，丙烯酸辛酯7‑9份，双甲基丙烯酸二丁基锡5‑10份，纳米高岭土10‑20份，引发剂1‑2份，交联剂3‑5份。
【技术特征摘要】
1.一种抗冲击耐高温有机玻璃，其特征在于，其原料按重量份包括：甲基丙烯酸甲酯70-75份，丙烯酸丁酯7-9份，丙烯酸辛酯7-9份，双甲基丙烯酸二丁基锡5-10份，纳米高岭土10-20份，引发剂1-2份，交联剂3-5份。2.根据权利要求1所述抗冲击耐高温有机玻璃，其特征在于，甲基丙烯酸甲酯、丙烯酸丁酯、丙烯酸辛酯、双甲基丙烯酸二丁基锡的重量比为75：7：7：10。3.根据权利要求1或2所述抗冲击耐高温有机玻璃，其特征在于，甲基丙烯酸甲酯与纳米高岭土的重量比为75：15。4.根据权利要求1-3任一项所述抗冲击耐高温有机...
【专利技术属性】
技术研发人员：杨艳，顾承永，
申请(专利权)人：蚌埠承永玻璃制品有限公司，
类型：发明
国别省市：安徽,34