The invention relates to a macromolecularization method of a stilbene diazo dye. An amphiphilic compound containing fluorescein group and tertiary amine structure was synthesized, which can be used as an initiator for free radical polymerization. Its tertiary amine can react with potassium persulfate at room temperature to produce active free radicals for many times. The oil-soluble monomer vinyl acetate polymerization was initiated at the water/oil interface. The obtained product was hydrolyzed to obtain polyvinyl alcohol with hydrophilic chain segments. Compounds, thus realizing the purpose of macromolecule polymerization of stilbene diazo dyes. This mode can make the functionalization and polymerization not interfere with each other, with high degree of freedom of operation, many kinds of products, mild conditions of polymerization, without organic solvents and emulsifiers, and meet the requirements of green chemistry.
【技术实现步骤摘要】
一种二苯乙烯双偶氮染料的高分子化方法
本专利技术涉及功能高分子材料合成
，尤其是一种二苯乙烯双偶氮染料的高分子化制备技术，通过该新的合成技术可将二苯乙烯双偶氮染料分子引入到聚烯烃类高分子材料中，从而产生一类新的功能高分子材料及其相关的应用技术。
技术介绍
聚烯烃是一类非常重要的通用高分子材料，是由若干种烯烃单体通过自由基聚合而形成，针对不同的用途，依据单体共聚合技术实现结构可调，因而应用广泛。引发剂在高分子材料制备中是必不可少的，通常的引发剂是一类能产生自由基的化合物，如油溶性的过氧类、偶氮类引发剂以及水溶性的过硫酸盐等，引发剂的使用必须要与具体的聚合反应环境相配合，传统上认为，一种引发剂只对应某一类的聚合反应，引发剂的结构与功能相对来说比较简单。如果对引发剂的结构和功能进行设计和改造，完全可以使自由基聚合反应发挥出更强的功能，所获得的聚合物材料具有更大的应用价值。直接冻黄G是一种具有二苯乙烯双偶氮结构的直接染料，含有亲水的磺酸基团，外观为橘黄色粉末，溶于水中为金黄色至黄色溶液，水溶液低于15℃时有冻状沉淀物析出，故称冻黄。其染色力强，耐晒，是纺织工业上一种...
【技术保护点】
1.一种二苯乙烯双偶氮染料的高分子化方法，其特征在于使用如下结构的功能性引发剂：
【技术特征摘要】
1.一种二苯乙烯双偶氮染料的高分子化方法，其特征在于使用如下结构的功能性引发剂：所述的高分子化方法的操作步骤依次为：1)将18.0g功能性引发剂分散于800mL水中形成乳化液，浓度控制在2.0～2.5wt.％范围；2)将油溶性单体醋酸乙烯酯加入到乳化液中，单体与引发剂的重量比在1∶1～4∶1范围；充分搅拌后加入过硫酸钾固体粉末，其用量为投入引发剂重量的2.0～3.0％，5～10分钟后聚合反应发生，体系温度有所上升，并很快形...
【专利技术属性】
技术研发人员：李艳，张瑞丰，李赛赛，肖通虎，龙能兵，
申请(专利权)人：宁波大学，
类型：发明
国别省市：浙江,33