The invention relates to a preparation method of active boron nitride fiber with high specific surface area. The method used melamine and boric acid as raw materials and hexamethylenetetramine as surfactant to prepare activated boron nitride fibers in three steps. The prepared activated boron nitride fibers have uniform size, good aspect ratio, low crystallinity, many surface defects, and many active functional groups. At the same time, the activated boron nitride fibers have high specific surface area and pore volume, which provide high adsorption capacity for its adsorption performance. The method is simple, cheap and easy to obtain, non-toxic, and the specific surface area of the product is stable. It has excellent performance in adsorbing organic dyes, metal ions and greenhouse gases.
【技术实现步骤摘要】
一种高比表面积的活性氮化硼纤维的制备方法
本专利技术涉及吸附领域，具体为一种高比表面积的活性多孔氮化硼纤维的方法。
技术介绍
氮化硼(BN)是一种重要的陶瓷材料，因为它具有与石墨相同的六方结构而被称为“白色石墨”。氮化硼材料的优异性能包括硬度极高，介电常数低，机械强度高，低密度大，熔点高，耐腐蚀性好和抗氧化性，因此氮化硼在制造耐火材料，润滑油，保护和光学涂层，切割工具，研磨材料，陶瓷复合材料，电子设备和电气绝缘子等方面具有巨大的潜力。氮化硼纳米材料主要包括氮化硼纳米球、氮化硼纳米片、氮化硼纳米管和氮化硼纤维。多孔氮化硼纤维是一种新型多孔材料，内部由相互贯通或封闭的孔洞构成，具有高比表面积和丰富的孔道结构，同时化学性能稳定、热导率高、绝缘性能良好，且具有疏水的特性。另外，多孔氮化硼材料具有特殊的氢化性质和选择吸附性能，在储氢、气体吸附和分离领域具有很大的应用潜力。因此多孔氮化硼材料的纯度、比表面积、孔径分布、表面缺陷及官能团数量对氮化硼材料的储氢、吸附和分离性能有着重要的影响。活性氮化硼的出现使得多孔氮化硼的储氢、吸附和分离性能进一步提高，目前活化活性氮化硼的方法主...
【技术保护点】
1.一种高比表面积的活性氮化硼纤维的制备方法，其特征为该方法包括以下步骤：（1）将三聚氰胺和硼酸放入盛有去离子水的容器中，然后将其放入水浴锅中，水浴温度区间为70~90 ℃，搅拌，得到澄清透明溶液；其中，三聚氰胺的浓度为0.1~0.2 mol/L，硼酸浓度为0.2~0.4 mol/L；摩尔比三聚氰胺：硼酸=1:2；（2）在步骤（1）得到的溶液中加入六次甲基四胺，继续搅拌，然后反应20~40 min，得到澄清溶液；其中，摩尔比为三聚氰胺：六次甲基四胺=6:1~2；（3）将步骤（2）得到的澄清溶液自然降温至40 ℃，并保持9~13 h，得到白色絮状沉淀；（4）将步骤（3）中得到...
【技术特征摘要】
1.一种高比表面积的活性氮化硼纤维的制备方法，其特征为该方法包括以下步骤：（1）将三聚氰胺和硼酸放入盛有去离子水的容器中，然后将其放入水浴锅中，水浴温度区间为70~90℃，搅拌，得到澄清透明溶液；其中，三聚氰胺的浓度为0.1~0.2mol/L，硼酸浓度为0.2~0.4mol/L；摩尔比三聚氰胺：硼酸=1:2；（2）在步骤（1）得到的溶液中加入六次甲基四胺，继续搅拌，然后反应20~40min，得到澄清溶液；其中，摩尔比为三聚氰胺：六次甲基四胺=6:1~2；（3）将步骤...
【专利技术属性】
技术研发人员：唐成春，王德坤，王晨阳，薛彦明，
申请(专利权)人：河北工业大学，
类型：发明
国别省市：天津,12