The invention relates to an additive for improving cracking and water absorption of alkali slag cement stone and its application method, belonging to the technical field of building materials. The additive is composed of 40 to 70 parts of stearate, 10 to 20 parts of alkali slag retarder, 5 to 10 parts of organosilicon and 45 to 60 parts of calcium hydroxide according to its weight. Through the rational mixing of the components and the limit of their dosage, the additive can significantly improve the cracking problem of alkali slag cement stone, and then reduce the water absorption of alkali slag cement stone. Moreover, the additive has no negative impact on the mechanical properties of alkali slag cement stone. Its synthesis method is simple, raw materials are easy to obtain, and it is suitable for industrial production.
【技术实现步骤摘要】
一种改善碱矿渣水泥石开裂和吸水的外加剂及其使用方法
本专利技术属于建筑材料
，具体涉及一种改善碱矿渣水泥石开裂和吸水的外加剂及其使用方法。
技术介绍
碱矿渣水泥(AAS)是用碱金属化合物激发磨细粒化高炉矿渣得到的一种新型水硬性胶凝材料。碱矿渣水泥石，强度高且耐腐蚀，其耐火性、抗氯盐侵蚀性等均优于通用硅酸盐水泥，但其干燥收缩较大，比通用硅酸盐水泥更容易造成浆体、砂浆或混凝土的开裂，导致其吸水性增大，最终诱发各种耐久性问题，这已成为制约碱矿渣水泥被广泛应用的技术“瓶颈”。由于碱矿渣水泥水化过程复杂，有序性较差的水化产物在形态及结构方面存在大量微观缺陷，这既是碱矿渣水泥石易变形，开裂的问题来源，也是其吸水性大的根本原因之一。目前，解决碱矿渣水泥石开裂和吸水的方法如下：(1)掺入金属离子膨胀剂，如通用硅酸盐水泥膨胀剂，其机理是形成具有较强膨胀作用的钙矾石，而在碱矿渣水泥高碱环境中，钙矾石难以形成，达不到预期膨胀的效果，且同时添加的Ca(OH)2会使碱矿渣水泥的凝结过快。(2)掺入减缩剂，以降低孔溶液的表面张力，但用于通用硅酸盐水泥的减缩剂在碱矿渣高碱环境中的适应性和...
【技术保护点】
1.一种改善碱矿渣水泥石开裂和吸水的外加剂，其特征在于，按质量份计，所述外加剂由如下组份组成：硬脂酸盐40‑70份、碱矿渣缓凝剂10‑20份、有机硅5‑10份、氢氧化钙45‑60份。
【技术特征摘要】
1.一种改善碱矿渣水泥石开裂和吸水的外加剂，其特征在于，按质量份计，所述外加剂由如下组份组成：硬脂酸盐40-70份、碱矿渣缓凝剂10-20份、有机硅5-10份、氢氧化钙45-60份。2.如权利要求1所述的一种改善碱矿渣水泥石开裂和吸水的外加剂，其特征在于，按质量份计，所述外加剂由如下组份组成：硬脂酸盐40份、碱矿渣缓凝剂10份、有机硅5份、氢氧化钙45份。3.如权利要求1所述的一种改善碱矿渣水泥石开裂和吸水的外加剂，其特征在于，按质量份计，所述外加剂由如下组份组成：硬脂酸盐50份、碱矿渣缓凝剂12份、有机硅6份、氢氧化钙50份。4.如权利要求1所述的一种改善碱矿渣水泥石开裂和吸水的外加剂，其特征在于，按质量份计，所...
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。