The invention discloses a mixed-based biomass activated carbon and a preparation method thereof. In the invention, grapefruit peel and walnut shell are mixed at a mass ratio of 3:7, and used as precursor of activated carbon. A new mixed-based biomass activated carbon is prepared by chemical activation method, adding activator and pyrolysis at high temperature. Compared with the biomass activated carbon and commercial activated carbon prepared from a single raw material, the adsorption performance of the new mixed-based biomass activated carbon is better, which shows that the new mixed-based biomass activated carbon can make up for the defects of the single raw material as the precursor of activated carbon, and has a certain commercial value. At the same time, this preparation scheme also provides a new idea for the environmental protection and utilization of biomass wastes.
【技术实现步骤摘要】
一种混合基生物质活性炭及其制备方法
本专利技术属于活性炭制备领域，尤其涉及一种混合基生物质活性炭及其制备方法。
技术介绍
活性炭因其发达的孔结构和较大的表面积而具有优异的吸附性能，且物理化学性质稳定，具有良好的循环再生性。因此，活性炭被广泛应用于液体和气体的净化领域，消耗量大。但是传统的活性炭制备原料一般为石油、焦煤、沥青以及木材等储量有限的不可再生资源，在全球资源紧张的大形势下传统的制备方法显然不利于环境的可持续发展。另一方面，高质量的活性炭价格昂贵，且再生效率较低，严重制约其大规模的工业化应用可用于制备活性炭的生物质原料按照硬度划分有硬质和软质两类：软质类包括稻壳、花生壳、柚子皮、玉米秸秆、甘蔗渣等；硬质类包括核桃壳、杏核、椰壳、开心果壳等果类核、壳。但是以单一的原料作为活性炭前体存在缺陷。例如，软质生物质材料有相对较高的灰分，半纤维素含量较低导致其具有较低的表观密度；核壳类硬质生物质材料活性炭制备的预处理环节能耗较大，并且年产量有限。目前，我国用于制备生物质活性炭的原料以果壳类居多，主要有椰壳、核桃壳、松籽壳等。但受果壳类原料来源的限制，致使目前生物质活性炭...
【技术保护点】
1.一种混合基生物质活性炭的制备方法，其特征在于，包括如下步骤：（1）制备生物质炭前体：将柚子皮和核桃壳清理、干燥、磨成粉末，其中柚子皮和核桃壳的质量比为3：7，混合均匀；（2）采用化学活化法制备混合基生物质活性炭：以质量分数为40%的磷酸溶液为活化剂，步骤（1）制备的生物质炭前体与活化剂中纯磷酸的质量比为1:3；生物质炭前体室温下在活化剂中浸渍18小时，将浸渍过的材料烘干至液面消失；放入马弗炉中热解，热解温度为300℃，热解时间为1小时，待产物自然冷却至室温后，取出，磨成粉末，用蒸馏水反复洗涤直到滤液呈中性；将洗涤好的产物烘干、再次粉碎、冷却、采用200目的筛子过筛，存放于干燥器中。
【技术特征摘要】
1.一种混合基生物质活性炭的制备方法，其特征在于，包括如下步骤：（1）制备生物质炭前体：将柚子皮和核桃壳清理、干燥、磨成粉末，其中柚子皮和核桃壳的质量比为3：7，混合均匀；（2）采用化学活化法制备混合基生物质活性炭：以质量分数为40%的磷酸溶液为活化剂，步骤（1）制备的生物质炭前体与活化剂中纯磷酸的质量比为1:3；生物...
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。